Název v původním jazyce

Influence of Surface Layers on Structure Stability and Product Qualities of Nickel-Base Superalloys

Popis výsledku v původním jazyce

Nickel base-superalloys are favourite materials for most exposed parts of aircraft engines. Apart from the development of new materials based on strengthening effects of ordered ă' phase, their surface protection is most pursued problem in high temperature materials research. The constructional parts of gas-engine turbines (blades, discs and shaft of high pressure turbine) are exposure to high dynamic stress (fatigue processes and creep) and various temperatures in dioxide-corrosion condition (hot corroosion, oxidation and erosion). The suitable protection against hot corrosion and erosion are surface coatings [5] especially codeposition of Al and Si by pack cementation process. The technology of Al-Si protective layers production is defined in literature [2]. This paper aims to study the diffusion processes and the phase transformation of Al-Si protective layers and the layer - line (between Al-Si layer and basic material ZHS6K).

Název v anglickém jazyce

Influence of Surface Layers on Structure Stability and Product Qualities of Nickel-Base Superalloys

Popis výsledku anglicky

Nickel base-superalloys are favourite materials for most exposed parts of aircraft engines. Apart from the development of new materials based on strengthening effects of ordered ă' phase, their surface protection is most pursued problem in high temperature materials research. The constructional parts of gas-engine turbines (blades, discs and shaft of high pressure turbine) are exposure to high dynamic stress (fatigue processes and creep) and various temperatures in dioxide-corrosion condition (hot corroosion, oxidation and erosion). The suitable protection against hot corrosion and erosion are surface coatings [5] especially codeposition of Al and Si by pack cementation process. The technology of Al-Si protective layers production is defined in literature [2]. This paper aims to study the diffusion processes and the phase transformation of Al-Si protective layers and the layer - line (between Al-Si layer and basic material ZHS6K).

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GD106%2F05%2FH008" target="_blank" >GD106/05/H008: Víceúrovňový design pokrokových materiálů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Juniormat 05

ISBN

80-214-2984-4

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

271-274

Název nakladatele

CSNMT

Místo vydání

Praha

Místo konání akce

Brno

Datum konání akce

20. 9. 2005

Typ akce podle státní příslušnosti

CST - Celostátní akce

Kód UT WoS článku

—