Název v původním jazyce

Failure behavior of coated materials

Popis výsledku v původním jazyce

Results concerning the influence of a through coating crack on the substrate failure are reported. The problem is studied under the assumptions corresponding to small scale yielding conditions and calculations are performed by the finite element method.An approximate approach based on calculations of crack mouth opening displacement for thin protective layers is suggested. It is concluded that in the case of a stiffer coating on a more compliant substrate, the through coating cracks represent dangerousstress concentrators, and as a consequence of elastic mismatch of both materials, the critical applied stress for substrate failure decreases. Traditional approaches may have underestimated this effect and estimations of the service life of coated structures neglecting this phenomenon could lead to non-conservative values, with unexpected failures.

Název v anglickém jazyce

Failure behavior of coated materials

Popis výsledku anglicky

Results concerning the influence of a through coating crack on the substrate failure are reported. The problem is studied under the assumptions corresponding to small scale yielding conditions and calculations are performed by the finite element method.An approximate approach based on calculations of crack mouth opening displacement for thin protective layers is suggested. It is concluded that in the case of a stiffer coating on a more compliant substrate, the through coating cracks represent dangerousstress concentrators, and as a consequence of elastic mismatch of both materials, the critical applied stress for substrate failure decreases. Traditional approaches may have underestimated this effect and estimations of the service life of coated structures neglecting this phenomenon could lead to non-conservative values, with unexpected failures.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GA101%2F05%2F0320" target="_blank" >GA101/05/0320: Řešení obecných koncentrátorů napětí v anisotropních heterogenních prostředích pomocí kombinace MKP a techniky spojitě rozložených dislokací</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

10 th International Conference on Numerical Methods in Continuum Mechanics

ISBN

80-969165-4-8

ISSN

—

e-ISSN

—

Počet stran výsledku

2

Strana od-do

47-48

Název nakladatele

University of Zilina

Místo vydání

Žilina

Místo konání akce

Žilina

Datum konání akce

23. 8. 2005

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—