Computational Modelling of Bimaterial Interface Failure in View of Rubber-Steel Interface

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F05%3APU91002" target="_blank" >RIV/00216305:26210/05:PU91002 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Computational Modelling of Bimaterial Interface Failure in View of Rubber-Steel Interface

Popis výsledku v původním jazyce

This paper presents a brief review of selected approaches used for computational modelling of bimaterial interface failure and for evaluation of interface failure resistance. Attention is paid to the approaches that assume absence of initial interface crack. The applicability of such approaches to rubber-steel interface failure evaluation is discussed in the paper. The approach based on the so called cohesive zone model is preferred and demonstrated by an example of computational modelling of rubber-steel interface failure during a peel-test. The results of peel-test computational modelling are presented. The influence of cohesive zone element number on the results is also analysed. The results are consistent with experimental data.

Název v anglickém jazyce

Computational Modelling of Bimaterial Interface Failure in View of Rubber-Steel Interface

Popis výsledku anglicky

This paper presents a brief review of selected approaches used for computational modelling of bimaterial interface failure and for evaluation of interface failure resistance. Attention is paid to the approaches that assume absence of initial interface crack. The applicability of such approaches to rubber-steel interface failure evaluation is discussed in the paper. The approach based on the so called cohesive zone model is preferred and demonstrated by an example of computational modelling of rubber-steel interface failure during a peel-test. The results of peel-test computational modelling are presented. The influence of cohesive zone element number on the results is also analysed. The results are consistent with experimental data.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)<br>V - Vyzkumna aktivita podporovana z jinych verejnych zdroju<br>N - Vyzkumna aktivita podporovana z neverejnych zdroju

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Engineering Mechanics

ISSN

1802-1484

e-ISSN

—

Svazek periodika

12

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

13

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—