Název v původním jazyce

Numerical analysis of a transversal crack in a steel slab

Popis výsledku v původním jazyce

This paper deals with the causes of a transversal crack in a steel slab with a 1300x145 mm cross-section by means of two numerical models. Samples were taken from and around the crack in order to analyze the concentration, as well as the chemical heterogeneity of the constituent elements and impurities. Simultaneously, the concentration of elements at the surface of the crack was measured after the crack was opened. The heterogeneity of elements was analyzed by the JEOL JXA 8600/KEVEX device. The measurrement results were processed using mathematical statistics. The chemical heterogeneity of elements in the steel matrix around the crack, and at the crack surface, had been evaluated with the help of heterogeneity parameters, i.e. the arithmetic mean ofconcentration, the standard deviation of concentration and the index of heterogeneity of the analyzed elements. The results proved that there was an internal crack initiating immediately below the solidus temperature and consecutively prop

Název v anglickém jazyce

Numerical analysis of a transversal crack in a steel slab

Popis výsledku anglicky

This paper deals with the causes of a transversal crack in a steel slab with a 1300x145 mm cross-section by means of two numerical models. Samples were taken from and around the crack in order to analyze the concentration, as well as the chemical heterogeneity of the constituent elements and impurities. Simultaneously, the concentration of elements at the surface of the crack was measured after the crack was opened. The heterogeneity of elements was analyzed by the JEOL JXA 8600/KEVEX device. The measurrement results were processed using mathematical statistics. The chemical heterogeneity of elements in the steel matrix around the crack, and at the crack surface, had been evaluated with the help of heterogeneity parameters, i.e. the arithmetic mean ofconcentration, the standard deviation of concentration and the index of heterogeneity of the analyzed elements. The results proved that there was an internal crack initiating immediately below the solidus temperature and consecutively prop

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Teorie a praxe výroby a zpracování oceli

ISBN

80-86840-15-8

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

18-24

Název nakladatele

Tanger Ostrava, VŠB TU Ostrava

Místo vydání

Tanger Ostrava, VŠB TU Ostrava Keltičkova 62,

Místo konání akce

Rožnov pod Radhoštěm

Datum konání akce

4. 4. 2006

Typ akce podle státní příslušnosti

CST - Celostátní akce

Kód UT WoS článku

—