Analýza příčné trhliny v ocelové bramě

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61989100%3A27360%2F07%3A00016093" target="_blank" >RIV/61989100:27360/07:00016093 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Analysis of a transversal crack in a steel slab

Popis výsledku v původním jazyce

This paper deals with the causes of a transversal crack in a steel slab with an l300xl45 mm cross-section by means of results from two models. Samples were taken from and around the crack in order to analyze the concentration (chemical heterogeneity) ofthe selected elements. Simultaneously, the concentration of elements at the surface of the crack was measured after the crack was opened. The chemical heterogeneity of elements was analyzed by means of the JEOL JXA 8600/KEVEX analytical equipment. The measurement results were processed using mathematical statistics procedures. The results proved that there was an internal crack initiating immediately below the curve of the solid-state temperature and consecutively propagating.

Název v anglickém jazyce

Analysis of a transversal crack in a steel slab

Popis výsledku anglicky

This paper deals with the causes of a transversal crack in a steel slab with an l300xl45 mm cross-section by means of results from two models. Samples were taken from and around the crack in order to analyze the concentration (chemical heterogeneity) ofthe selected elements. Simultaneously, the concentration of elements at the surface of the crack was measured after the crack was opened. The chemical heterogeneity of elements was analyzed by means of the JEOL JXA 8600/KEVEX analytical equipment. The measurement results were processed using mathematical statistics procedures. The results proved that there was an internal crack initiating immediately below the curve of the solid-state temperature and consecutively propagating.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Materials Sctructure and Micromechanics of Fracture

ISBN

978-80-214-3434-9

ISSN

—

e-ISSN

—

Počet stran výsledku

1

Strana od-do

51-51

Název nakladatele

Vysoká škola technická

Místo vydání

Brno

Místo konání akce

—

Datum konání akce

—

Typ akce podle státní příslušnosti

—

Kód UT WoS článku

—