Určení parametrů keramického materiálu z destrukcí keramických hlavic

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F06%3APU62656" target="_blank" >RIV/00216305:26210/06:PU62656 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

CALCULATION OF THE CERAMICS MATERIAL PARAMETERS FROM THE TESTING DESTRUCTIONS OF THE HEADS

Popis výsledku v původním jazyce

This paper deals with increasing of the computation modelling level of the reliability problem of ceramic heads of total hip joint endoprostheses. The solution to this problem was invoked by recent more frequent failures of these heads in clinical practice. Results of computational and experimental modelling have shown a substantial influence of shape deviations in the conical connection between stem and head on the initiation of ceramic head fractures. The fracture probability was evaluated step by steep for various macroscopic shape deviations in the conical connection and then for microscopic shape deviations superposed on the macroscopic deviations. The solution to the problem of ceramic head reliability requires realization of two computational models: one for determination of stress states and another one for evaluation of the fracture probability. Material characteristics of ceramics used in fracture probability evaluation have been determined by a three-point-bending test till

Název v anglickém jazyce

CALCULATION OF THE CERAMICS MATERIAL PARAMETERS FROM THE TESTING DESTRUCTIONS OF THE HEADS

Popis výsledku anglicky

This paper deals with increasing of the computation modelling level of the reliability problem of ceramic heads of total hip joint endoprostheses. The solution to this problem was invoked by recent more frequent failures of these heads in clinical practice. Results of computational and experimental modelling have shown a substantial influence of shape deviations in the conical connection between stem and head on the initiation of ceramic head fractures. The fracture probability was evaluated step by steep for various macroscopic shape deviations in the conical connection and then for microscopic shape deviations superposed on the macroscopic deviations. The solution to the problem of ceramic head reliability requires realization of two computational models: one for determination of stress states and another one for evaluation of the fracture probability. Material characteristics of ceramics used in fracture probability evaluation have been determined by a three-point-bending test till

Druh

D - Stať ve sborníku

CEP obor

BO - Biofyzika

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Engineering Mechanics 2006

ISBN

80-86246-27-2

ISSN

—

e-ISSN

—

Počet stran výsledku

2

Strana od-do

76-77

Název nakladatele

ÚTAM AV ČR

Místo vydání

Svratka

Místo konání akce

Svratka

Datum konání akce

15. 5. 2006

Typ akce podle státní příslušnosti

CST - Celostátní akce

Kód UT WoS článku

—