Synthesis, structure and oxygen thermally programmed desorption spectra of La1-xCaxAlyFe1-yO3-d perovskites

Popis výsledku v původním jazyce

Perovskites La1-xCaxAlyFe1-yO3-d (x, y = 0 to 1) were prepared by high-temperature solid-state synthesis based on mixtures of oxides produced by colloidal milling. The XRD analysis showed that perovskites La0.5Ca0.5AlyFe1-yO3-d with a high Fe content (1- y = 0.8-1.0) were of orthorhombic structure, perovskites with a medium Fe content (1 - y = 0.8-0.5) were of rhombohedral structure, and perovskite with the lowest Fe content (1 - y = 0.2) were of cubic structure. Thermally programmed desorption (TPD) of oxygen revealed that chemical desorption of oxygen in the temperature range from 200 to 1000 degC had proceeded in the two desorption peaks. The low-temperature alfa-peak (in the 200-550 degC temperature range) was brought about by oxygen liberated from oxygen vacancies; the high-temperature beta-peak (in the 550-1000 degC temperature range) corresponded to the reduction of Fe4+ to Fe3+. The chemidesorption oxygen capacity increased with increasing Ca content and decreased with increas

Název v anglickém jazyce

Synthesis, structure and oxygen thermally programmed desorption spectra of La1-xCaxAlyFe1-yO3-d perovskites

Popis výsledku anglicky

Perovskites La1-xCaxAlyFe1-yO3-d (x, y = 0 to 1) were prepared by high-temperature solid-state synthesis based on mixtures of oxides produced by colloidal milling. The XRD analysis showed that perovskites La0.5Ca0.5AlyFe1-yO3-d with a high Fe content (1- y = 0.8-1.0) were of orthorhombic structure, perovskites with a medium Fe content (1 - y = 0.8-0.5) were of rhombohedral structure, and perovskite with the lowest Fe content (1 - y = 0.2) were of cubic structure. Thermally programmed desorption (TPD) of oxygen revealed that chemical desorption of oxygen in the temperature range from 200 to 1000 degC had proceeded in the two desorption peaks. The low-temperature alfa-peak (in the 200-550 degC temperature range) was brought about by oxygen liberated from oxygen vacancies; the high-temperature beta-peak (in the 550-1000 degC temperature range) corresponded to the reduction of Fe4+ to Fe3+. The chemidesorption oxygen capacity increased with increasing Ca content and decreased with increas

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/OC%20525.10" target="_blank" >OC 525.10: Příprava a vlastnosti keramických materiálů s iontovou nebo iontově-elektronovou vodivostí</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of the European Ceramic Society

ISSN

0955-2219

e-ISSN

—

Svazek periodika

26

Číslo periodika v rámci svazku

14

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

6

Strana od-do

2999-3004

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—