Název v původním jazyce
High temperature high cycle fatigue behavior of Ni base superalloy IN 713 LC at tensile mean stress
Popis výsledku v původním jazyce
High-cycle fatigue/creep behaviour of cast nickel base superalloy IN713LC was experimentally examined at 800 C in air. Experiments were aimed on determination of cyclic creep rate, time to fracture, kind and mode of damage. An attempt has been made to explain the cyclic creep behaviour by a balance between an effect of decrease of plastic strain response with increasing strain rate in a loading cycle and an accelerating effect of the cyclic plasticity on the development of unidirectional plastic strain.Three types of fatigue crack initiation were observed: long crystallographic Stage I surface initiation, internal crystallographic initiation related to structural defects and initiation on defect followed by Stage II crack propagation.
Název v anglickém jazyce
High temperature high cycle fatigue behavior of Ni base superalloy IN 713 LC at tensile mean stress
Popis výsledku anglicky
High-cycle fatigue/creep behaviour of cast nickel base superalloy IN713LC was experimentally examined at 800 C in air. Experiments were aimed on determination of cyclic creep rate, time to fracture, kind and mode of damage. An attempt has been made to explain the cyclic creep behaviour by a balance between an effect of decrease of plastic strain response with increasing strain rate in a loading cycle and an accelerating effect of the cyclic plasticity on the development of unidirectional plastic strain.Three types of fatigue crack initiation were observed: long crystallographic Stage I surface initiation, internal crystallographic initiation related to structural defects and initiation on defect followed by Stage II crack propagation.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2006
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Víceúrovňový design pokrokových materiálů
ISBN
80-239-8271-0
ISSN
—
e-ISSN
—
Počet stran výsledku
8
Strana od-do
119-126
Název nakladatele
AVČR, Brno
Místo vydání
Brno
Místo konání akce
Ústav fyziky materiálů AVČR, Žižkova 22, B
Datum konání akce
30. 11. 2006
Typ akce podle státní příslušnosti
CST - Celostátní akce
Kód UT WoS článku
—