Effect of tensile dwell on high-temperature low-cycle fatigue and fracture behaviour of cast superalloy MAR-M247

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F17%3A00482087" target="_blank" >RIV/68081723:_____/17:00482087 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.engfracmech.2017.04.002" target="_blank" >http://dx.doi.org/10.1016/j.engfracmech.2017.04.002</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.engfracmech.2017.04.002" target="_blank" >10.1016/j.engfracmech.2017.04.002</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of tensile dwell on high-temperature low-cycle fatigue and fracture behaviour of cast superalloy MAR-M247

Popis výsledku v původním jazyce

Hot isostatically-pressed, nickel-based superalloy MAR-M247 was tested under fatigue and creep-fatigue conditions. Continuous cycling and cycling with 10 min tensile dwells in each cycle were applied in symmetrical strain control cycle with constant total strain amplitude at 900 °C in air. Cyclic hardening/softening curves, cyclic stress-strain curves and fatigue life curves were obtained. The introduction of tensile dwells resulted in lower fatigue life in total strain representation. Surface relief, specimen sections and fracture surface observations revealed crack initiation sites, crack density and crack paths, and help to clarify the effect of dwells on fatigue behaviour.

Název v anglickém jazyce

Effect of tensile dwell on high-temperature low-cycle fatigue and fracture behaviour of cast superalloy MAR-M247

Popis výsledku anglicky

Hot isostatically-pressed, nickel-based superalloy MAR-M247 was tested under fatigue and creep-fatigue conditions. Continuous cycling and cycling with 10 min tensile dwells in each cycle were applied in symmetrical strain control cycle with constant total strain amplitude at 900 °C in air. Cyclic hardening/softening curves, cyclic stress-strain curves and fatigue life curves were obtained. The introduction of tensile dwells resulted in lower fatigue life in total strain representation. Surface relief, specimen sections and fracture surface observations revealed crack initiation sites, crack density and crack paths, and help to clarify the effect of dwells on fatigue behaviour.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20306 - Audio engineering, reliability analysis

Projekt

<a href="/cs/project/GA15-20991S" target="_blank" >GA15-20991S: Plazmová depozice, strukturní a termomechanická stabilita environmentálních bariér</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Engineering Fracture Mechanics

ISSN

0013-7944

e-ISSN

—

Svazek periodika

185

Číslo periodika v rámci svazku

NOV

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

9

Strana od-do

92-100

Kód UT WoS článku

000415941400009

EID výsledku v databázi Scopus

2-s2.0-85018162275