Effect of tensile dwell on low cycle fatigue of cast superalloy Inconel 792-5A at 800°C

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F12%3A00371437" target="_blank" >RIV/68081723:_____/12:00371437 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216305:26210/12:PU94396

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of tensile dwell on low cycle fatigue of cast superalloy Inconel 792-5A at 800°C

Popis výsledku v původním jazyce

Effect of tensile dwell on low cycle fatigue of cast Inconel 792-5A is studied in symmetrical strain cycling at 800°C. Cyclic hardening/softening curves, cyclic stress-strain curves (CSSC) and fatigue life curves were obtained in continuous cycling and in cycling with tensile dwells. Dwells have slight effect on hardening/softening curves at high strain amplitudes. CSSC in cycling with dwells is shifted to lower stress amplitudes. No significant effect of dwells on Basquin curves is observed. Density ofslip markings in cintinuous cycling is significantly higher in comparison with cycling with dwells. Samples cycled with dwells are typical of high density of secondary cracks, although sporadic slip markings were also found.

Název v anglickém jazyce

Effect of tensile dwell on low cycle fatigue of cast superalloy Inconel 792-5A at 800°C

Popis výsledku anglicky

Effect of tensile dwell on low cycle fatigue of cast Inconel 792-5A is studied in symmetrical strain cycling at 800°C. Cyclic hardening/softening curves, cyclic stress-strain curves (CSSC) and fatigue life curves were obtained in continuous cycling and in cycling with tensile dwells. Dwells have slight effect on hardening/softening curves at high strain amplitudes. CSSC in cycling with dwells is shifted to lower stress amplitudes. No significant effect of dwells on Basquin curves is observed. Density ofslip markings in cintinuous cycling is significantly higher in comparison with cycling with dwells. Samples cycled with dwells are typical of high density of secondary cracks, although sporadic slip markings were also found.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Key Engineering Materials

ISSN

1013-9826

e-ISSN

—

Svazek periodika

488-489

Číslo periodika v rámci svazku

-

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

4

Strana od-do

735-738

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—