Low cycle fatigue with hold times of cast superalloy Inconel 792-5A at 800 °C

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F12%3A00387120" target="_blank" >RIV/68081723:_____/12:00387120 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Low cycle fatigue with hold times of cast superalloy Inconel 792-5A at 800 °C

Popis výsledku v původním jazyce

Effect of hold times on low cycle fatigue of cast Inconel 792-5A is studied in symmetrical cyclic straining at 800°C. Cyclic hardening/softening curves, development of mean stress, cyclic stress-strain curves (CSSC) and fatigue life curves were obtainedin continuous cycling and in cycling with tensile and compressive hold times. Hold times have slight effect on hardening/softening curves at high strain amplitudes. CSSC in cycling with hold times is shifted to lower stress amplitudes. Significant reduction of fatigue life was observed on Basquin curves in case of cycling with compressive hold times. Density of slip markings in continuous cycling is significantly higher in comparison with cyclic straining with hold times. High density of secondary cracks is typical for specimen surface cycled with tensile hold times, although sporadic slip markings were also found.

Název v anglickém jazyce

Low cycle fatigue with hold times of cast superalloy Inconel 792-5A at 800 °C

Popis výsledku anglicky

Effect of hold times on low cycle fatigue of cast Inconel 792-5A is studied in symmetrical cyclic straining at 800°C. Cyclic hardening/softening curves, development of mean stress, cyclic stress-strain curves (CSSC) and fatigue life curves were obtainedin continuous cycling and in cycling with tensile and compressive hold times. Hold times have slight effect on hardening/softening curves at high strain amplitudes. CSSC in cycling with hold times is shifted to lower stress amplitudes. Significant reduction of fatigue life was observed on Basquin curves in case of cycling with compressive hold times. Density of slip markings in continuous cycling is significantly higher in comparison with cyclic straining with hold times. High density of secondary cracks is typical for specimen surface cycled with tensile hold times, although sporadic slip markings were also found.

Druh

D - Stať ve sborníku

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

SEMDOK 2012

ISBN

978-80-554-0477-6

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

65-68

Název nakladatele

Žilinská univerzita

Místo vydání

Žilina

Místo konání akce

Terchová

Datum konání akce

25. 1. 2012

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—