Microstructure-aided Analysis of Fatigue Thresholds in Duplex Stainless Steel
Popis výsledku v původním jazyce
High fatigue threshold values of duplex ferritic-martensitic steels are interpreted by using a unified model of roughness- and plasticity induced crack closure. Complex metallographical and fractographical analysis was performed in order to obtain characteristics of tortuous crack paths produced by crack deflection and branching mainly at austenite/ferrite interfaces. Calculated values of effective thresholds are in a good agreement with experimental data. The total level of extrinsic toughening (closure + shielding) induced by the duplex microstructure was determined to be as much as 70% of measured fatigue threshold values. This is the main reason for the high resistance to propagation of long fatigue cracks in the near-threshold region.
Název v anglickém jazyce
Microstructure-aided Analysis of Fatigue Thresholds in Duplex Stainless Steel
Popis výsledku anglicky
High fatigue threshold values of duplex ferritic-martensitic steels are interpreted by using a unified model of roughness- and plasticity induced crack closure. Complex metallographical and fractographical analysis was performed in order to obtain characteristics of tortuous crack paths produced by crack deflection and branching mainly at austenite/ferrite interfaces. Calculated values of effective thresholds are in a good agreement with experimental data. The total level of extrinsic toughening (closure + shielding) induced by the duplex microstructure was determined to be as much as 70% of measured fatigue threshold values. This is the main reason for the high resistance to propagation of long fatigue cracks in the near-threshold region.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2008
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials Science Forum
ISSN
0255-5476
e-ISSN
—
Svazek periodika
567-568
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
4
Strana od-do
—
Kód UT WoS článku
000253516900021
EID výsledku v databázi Scopus
—