Analysis of Multiple Cracks in Thin Coating on Orthotropic Substrate

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F08%3APU75416" target="_blank" >RIV/00216305:26210/08:PU75416 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Analysis of Multiple Cracks in Thin Coating on Orthotropic Substrate

Popis výsledku v původním jazyce

The analysis addresses a typical failure development pattern consisting of a system of multiple surface cracks leading to and branching along or near the interface between the coating and the base material. The process is driven by thermal stresses. Dueto the high temperature gradients during the fabrication process, usually a net of surface cracks develops, which gives the appearance of a granular structure of the surface. A periodic array of parallel surface cracks is assumed. A ''unit cell'' or single cracked segment attached to the substrate is analyzed instead by assuming the channel cracks are spaced more or less uniformly and perfectly aligned in parallel in the transverse direction of the coating. The problem is solved using both FEM combinedwith the reciprocal theorem and the technique of distributed dislocations. Existing semi-analytical solution for singularities in anisotropic trimaterials is applied.

Název v anglickém jazyce

Analysis of Multiple Cracks in Thin Coating on Orthotropic Substrate

Popis výsledku anglicky

The analysis addresses a typical failure development pattern consisting of a system of multiple surface cracks leading to and branching along or near the interface between the coating and the base material. The process is driven by thermal stresses. Dueto the high temperature gradients during the fabrication process, usually a net of surface cracks develops, which gives the appearance of a granular structure of the surface. A periodic array of parallel surface cracks is assumed. A ''unit cell'' or single cracked segment attached to the substrate is analyzed instead by assuming the channel cracks are spaced more or less uniformly and perfectly aligned in parallel in the transverse direction of the coating. The problem is solved using both FEM combinedwith the reciprocal theorem and the technique of distributed dislocations. Existing semi-analytical solution for singularities in anisotropic trimaterials is applied.

Druh

D - Stať ve sborníku

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F06%2F0724" target="_blank" >GA106/06/0724: Mikrostrukturně indukované stínící efekty při porušování kompozitů s keramickou matricí</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Multilevel Approach to Fracture of Materials, Components and Structures

ISBN

9781617823190

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

170-177

Název nakladatele

VUTIUM Brno

Místo vydání

Czech Republic

Místo konání akce

Brno

Datum konání akce

2. 9. 2008

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—