Two-Step Sintering and Spark Plasma Sintering of Al2O3, ZrO2 and SrTiO3 Ceramics

Popis výsledku v původním jazyce

The influence of Two Step Sintering and Spark Plasma Sintering processes on the microstructure of three kinds of oxide ceramics was studied. Al2O3 (with initial particle size of 240 nm), ZrO2 (60 nm, stabilized with 3 mol%Y2O3) and SrTiO3 (50 nm) powderswere cold isostatically pressed and pressureless sintered with different heating regimes. It was found that the method of TSS does not bring about significant reduction of final grain size in Al2O3 and ZrO2 ceramics, but does reduce the grain size in perovskite SrTiO3 ceramics. Pressureless sintering of SrTiO3 leads only to 95%TD dense ceramics with the minimum grain size of 400 nm. In comparison, by SPS, with an applied uniaxial pressure of 200MPa, SrTiO3 ceramic of 98%TD dense with grain size of 80 nm was prepared.

Název v anglickém jazyce

Two-Step Sintering and Spark Plasma Sintering of Al2O3, ZrO2 and SrTiO3 Ceramics

Popis výsledku anglicky

The influence of Two Step Sintering and Spark Plasma Sintering processes on the microstructure of three kinds of oxide ceramics was studied. Al2O3 (with initial particle size of 240 nm), ZrO2 (60 nm, stabilized with 3 mol%Y2O3) and SrTiO3 (50 nm) powderswere cold isostatically pressed and pressureless sintered with different heating regimes. It was found that the method of TSS does not bring about significant reduction of final grain size in Al2O3 and ZrO2 ceramics, but does reduce the grain size in perovskite SrTiO3 ceramics. Pressureless sintering of SrTiO3 leads only to 95%TD dense ceramics with the minimum grain size of 400 nm. In comparison, by SPS, with an applied uniaxial pressure of 200MPa, SrTiO3 ceramic of 98%TD dense with grain size of 80 nm was prepared.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/OC%20102" target="_blank" >OC 102: Příprava elektrokeramiky z nanoprášků</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

INTEGRATED FERROELECTRICS

ISSN

1058-4587

e-ISSN

—

Svazek periodika

99

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

11

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—