Hodnocení zhouževnatění v důsledku visko-elastického přemostění trhliny u žáruvzdorných materiálů

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F08%3APU76619" target="_blank" >RIV/00216305:26210/08:PU76619 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68081723:_____/08:00324255

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Assessment of viscoelastic crack bridging toughening in refractory materials

Popis výsledku v původním jazyce

Viscoelastic bridges can be formed in refractory ceramics while cooling from high temperatures. Such bridges can shield crack tips, thus reducing the effective crack tip stress intensity factors leading to higher resistance to creep and thermal shock. The extent to which the crack tip stress intensity is reduced can be estimated from fracture mechanics models that include experimental measurement of crack bridging and microstructural parameters. In this paper a novel approach is proposed for the assessment of the effective crack bridging toughening from combining destructive and non-destructive test methods. Fracture toughness values were determined applying chevron notched specimen technique and surface damage of the specimen was monitored by image analysis. Different cordierite-mullite compositions characterized by different microstructure morphologies and crack propagation behaviour were investigated. A brief discussion about the correlation between thermo-mechanical properties, mic

Název v anglickém jazyce

Assessment of viscoelastic crack bridging toughening in refractory materials

Popis výsledku anglicky

Viscoelastic bridges can be formed in refractory ceramics while cooling from high temperatures. Such bridges can shield crack tips, thus reducing the effective crack tip stress intensity factors leading to higher resistance to creep and thermal shock. The extent to which the crack tip stress intensity is reduced can be estimated from fracture mechanics models that include experimental measurement of crack bridging and microstructural parameters. In this paper a novel approach is proposed for the assessment of the effective crack bridging toughening from combining destructive and non-destructive test methods. Fracture toughness values were determined applying chevron notched specimen technique and surface damage of the specimen was monitored by image analysis. Different cordierite-mullite compositions characterized by different microstructure morphologies and crack propagation behaviour were investigated. A brief discussion about the correlation between thermo-mechanical properties, mic

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F05%2F0495" target="_blank" >GA106/05/0495: Odezva a porušení křehkých materiálů při rázovém zatěžování</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of the European Ceramic Society

ISSN

0955-2219

e-ISSN

—

Svazek periodika

28

Číslo periodika v rámci svazku

10

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

11

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—