Creepové charakteristiky a mikrostruktura svarových spojů P23/P91
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F09%3APU81335" target="_blank" >RIV/00216305:26210/09:PU81335 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/25870807:_____/09:#0000136 RIV/25870807:_____/09:#0000161
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Creep Properties and Microstructure of P23/P91 Heterogeneous Welds
Popis výsledku v původním jazyce
Two designs of P23/P91 heterogeneous welds have been investigated. The filler material in the Weld A corresponded to the P91 steel, while in the Weld B the low alloy filler material of the P23 type was applied. Creep rupture tests have been carried out at 500, 550, 600 degrees C for times to rupture exceeding 50 000 hours. Optical microscopy investigations were performed on ruptured testpieces in order to reveal the effect of testing parameters on the preferred location of failure. Detailed TEM investigations were carried out in the individual weld zones of the selected P23/P91 cross,veld specimens after long-term creep exposure. Experimental data on minor phase evolution were compared to the results of thermodynamic (Thermocalc) and kinetic (Dictra) simulations.
Název v anglickém jazyce
Creep Properties and Microstructure of P23/P91 Heterogeneous Welds
Popis výsledku anglicky
Two designs of P23/P91 heterogeneous welds have been investigated. The filler material in the Weld A corresponded to the P91 steel, while in the Weld B the low alloy filler material of the P23 type was applied. Creep rupture tests have been carried out at 500, 550, 600 degrees C for times to rupture exceeding 50 000 hours. Optical microscopy investigations were performed on ruptured testpieces in order to reveal the effect of testing parameters on the preferred location of failure. Detailed TEM investigations were carried out in the individual weld zones of the selected P23/P91 cross,veld specimens after long-term creep exposure. Experimental data on minor phase evolution were compared to the results of thermodynamic (Thermocalc) and kinetic (Dictra) simulations.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/OC%20099" target="_blank" >OC 099: Creepové chování a mikrostrukturní stabilita nových 9-12%Cr ocelí pro elektrárny s nadkritickými parametry páry</a><br>
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2009
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
CREEP & FRACTURE IN HIGHTEMPERATURE COMPONRNTS: DESIGN & LIFE ASSESMENT ISSUES
ISBN
978-1-60595-005-1
ISSN
—
e-ISSN
—
Počet stran výsledku
9
Strana od-do
—
Název nakladatele
DESTECH PUBLICATIONS, INC
Místo vydání
LANCASTER, PA 17602-4967,USA
Místo konání akce
Zurich
Datum konání akce
21. 4. 2009
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000266610600116