Synthesis and oxygen transport properties of La0.2Sr0.8Fe1.xTixO3.(x = 0.2, 0.4) intended for syn-gas production

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F09%3APU81585" target="_blank" >RIV/00216305:26210/09:PU81585 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Synthesis and oxygen transport properties of La0.2Sr0.8Fe1.xTixO3.(x = 0.2, 0.4) intended for syn-gas production

Popis výsledku v původním jazyce

Perovskites in the system La0.2Sr0.8Fe1-xTixO3-d exhibit high stability at severe reducing conditions and high temperatures. Due to favourable transport properties they are possible candidates both in oxygen permeation applications and anodes in SOFCs. Here we report the processing and oxygen transport properties of two different compositions: La0.2Sr0.8Fe1-xTixO3-d (x = 0.2, 0.4). Single phase powders were synthesized by both spray pyrolysis (SP) and solid state reaction (SSR). The resulting average particle sizes (BET) ranged from 140 nm (SP) to 1090 nm (SSR). Bar shaped samples were prepared by cold isostatic pressing and pressure less sintered between 1200 and 1250oC for 8-12 hours. Final sintered densities ranged from 97 (SSR) to 99% (SP) and grain size was less than 1.5 um. The average thermal expansion coefficients (TEC) varied in the range (13.8 - 14.6) .10-6K-1 at 300-600C and (21.3 - 28.9) .10-6K-1 at 600-800C. Surface exchange coefficients (kchem) and bulk diffusion coeffici

Název v anglickém jazyce

Synthesis and oxygen transport properties of La0.2Sr0.8Fe1.xTixO3.(x = 0.2, 0.4) intended for syn-gas production

Popis výsledku anglicky

Perovskites in the system La0.2Sr0.8Fe1-xTixO3-d exhibit high stability at severe reducing conditions and high temperatures. Due to favourable transport properties they are possible candidates both in oxygen permeation applications and anodes in SOFCs. Here we report the processing and oxygen transport properties of two different compositions: La0.2Sr0.8Fe1-xTixO3-d (x = 0.2, 0.4). Single phase powders were synthesized by both spray pyrolysis (SP) and solid state reaction (SSR). The resulting average particle sizes (BET) ranged from 140 nm (SP) to 1090 nm (SSR). Bar shaped samples were prepared by cold isostatic pressing and pressure less sintered between 1200 and 1250oC for 8-12 hours. Final sintered densities ranged from 97 (SSR) to 99% (SP) and grain size was less than 1.5 um. The average thermal expansion coefficients (TEC) varied in the range (13.8 - 14.6) .10-6K-1 at 300-600C and (21.3 - 28.9) .10-6K-1 at 600-800C. Surface exchange coefficients (kchem) and bulk diffusion coeffici

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/OC09015" target="_blank" >OC09015: Příprava elektrokeramiky z nanoprášků-II</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of the European Ceramic Society

ISSN

0955-2219

e-ISSN

—

Svazek periodika

30

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

7

Strana od-do

—

Kód UT WoS článku

000272455600083

EID výsledku v databázi Scopus

—