Oscillation Marks and Hooks on the Surface of Concast Slabs and their Relation to Breakout

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F10%3APU87379" target="_blank" >RIV/00216305:26210/10:PU87379 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Oscillation Marks and Hooks on the Surface of Concast Slabs and their Relation to Breakout

Popis výsledku v původním jazyce

In the secondary-cooling zone, where the slab is beginning to straighten out the breakout of the steel can occur in points of increased local chemical and temperature heterogeneity of the steel, from increased tension as a result of the bending of the slab and also from a high local concentration of non-metal, slag inclusions. Especially dangerous are the changes in the chemical composition of the steel during the actual concasting. In the case of two melts one immediately after the other, this could lead to immediate interruption in the concasting and a breakout. The material, physical, chemical and technological parameters, which both melts differed in were determined. If the dimensionless analysis is applied for assessing and reducing the number ofthese parameters, then it is possible to express the level of risk of breakout as a function of five dimensionless criteria.

Název v anglickém jazyce

Oscillation Marks and Hooks on the Surface of Concast Slabs and their Relation to Breakout

Popis výsledku anglicky

In the secondary-cooling zone, where the slab is beginning to straighten out the breakout of the steel can occur in points of increased local chemical and temperature heterogeneity of the steel, from increased tension as a result of the bending of the slab and also from a high local concentration of non-metal, slag inclusions. Especially dangerous are the changes in the chemical composition of the steel during the actual concasting. In the case of two melts one immediately after the other, this could lead to immediate interruption in the concasting and a breakout. The material, physical, chemical and technological parameters, which both melts differed in were determined. If the dimensionless analysis is applied for assessing and reducing the number ofthese parameters, then it is possible to express the level of risk of breakout as a function of five dimensionless criteria.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2010

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Abstract Booklet 6th International Conference on Materials Structure and Micromechanics of Fracture MSMF 6

ISBN

978-80-214-4112-5

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

—

Název nakladatele

VUTIUM Brno

Místo vydání

Brno

Místo konání akce

Brno

Datum konání akce

28. 6. 2010

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—