Stress state analysis of sub-sized pre-cracked three-point-bend specimen

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F11%3APU95655" target="_blank" >RIV/00216305:26210/11:PU95655 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68081723:_____/11:00370099

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Stress state analysis of sub-sized pre-cracked three-point-bend specimen

Popis výsledku v původním jazyce

The contribution deals with finite element analysis of stress state in subsized precracked threepoint bend specimen (KLST). A studied material was Eurofer97 steel. The true stress-true strain curve was obtained from tensile test. The threepoint bend tests were carried out on plain and sidegrooved specimens at ambient temperature and were simulated using ABAQUS 6.10. The stress state in KLST specimen was compared with the stress state of standard specimen. The analysis confirmed the stress state in KLSTspecimens at the crack tip does not correspond to conditions of standard fracture toughness determination because loss of constraint.

Název v anglickém jazyce

Stress state analysis of sub-sized pre-cracked three-point-bend specimen

Popis výsledku anglicky

The contribution deals with finite element analysis of stress state in subsized precracked threepoint bend specimen (KLST). A studied material was Eurofer97 steel. The true stress-true strain curve was obtained from tensile test. The threepoint bend tests were carried out on plain and sidegrooved specimens at ambient temperature and were simulated using ABAQUS 6.10. The stress state in KLST specimen was compared with the stress state of standard specimen. The analysis confirmed the stress state in KLSTspecimens at the crack tip does not correspond to conditions of standard fracture toughness determination because loss of constraint.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

13th Conference Applied Mechanics 2011

ISBN

978-80-87434-03-1

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

203-206

Název nakladatele

Ústav fyziky materiálů AV ČR, v.v.i.

Místo vydání

Brno

Místo konání akce

Velké Bílovice

Datum konání akce

18. 4. 2011

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—