Stress state analysis of sub-sized pre-cracked three-point-bend specimen

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F12%3APU102912" target="_blank" >RIV/00216305:26210/12:PU102912 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68081723:_____/12:00385663

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Stress state analysis of sub-sized pre-cracked three-point-bend specimen

Popis výsledku v původním jazyce

The contribution deals with finite element analysis of stress state in sub-sized pre-cracked three-point bend specimen (KLST). A studied material was Eurofer97 steel. The true stress-true strain curve was obtained from tensile test. The three-point-bendtests were carried out on pre-cracked plain and side-grooved specimens at ambient temperature. Performed tests were simulated using FEA software ABAQUS 6.10. The stress state in KLST specimen was compared with the stress state of pre-cracked Charpy and 1T SENB. The analysis confirmed the stress state in KLST specimens at the crack-tip does not correspond to the stress state of standard fracture toughness determination because of loss of crack-tip and out-of-plane constraint.

Název v anglickém jazyce

Stress state analysis of sub-sized pre-cracked three-point-bend specimen

Popis výsledku anglicky

The contribution deals with finite element analysis of stress state in sub-sized pre-cracked three-point bend specimen (KLST). A studied material was Eurofer97 steel. The true stress-true strain curve was obtained from tensile test. The three-point-bendtests were carried out on pre-cracked plain and side-grooved specimens at ambient temperature. Performed tests were simulated using FEA software ABAQUS 6.10. The stress state in KLST specimen was compared with the stress state of pre-cracked Charpy and 1T SENB. The analysis confirmed the stress state in KLST specimens at the crack-tip does not correspond to the stress state of standard fracture toughness determination because of loss of crack-tip and out-of-plane constraint.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Engineering Mechanics

ISSN

1802-1484

e-ISSN

—

Svazek periodika

2012(19)

Číslo periodika v rámci svazku

2/3

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

9

Strana od-do

121-129

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—