In-situ magnetic nano-patterning of Fe films grown on Cu(100)

Popis výsledku v původním jazyce

Metastable paramagnetic face-centered cubic (fcc) Fe films grown on a Cu(100) single crystal at room temperature can be transformed to the ferromagnetic body-centered cubic (bcc) structure by ion irradiation. We have employed this technique to write small ferromagnetic patches by Ar irradiation through a gold coated SiN mask with regularly arranged 80-nm diameter holes, which as placed on top of the as-prepared fcc Fe films. Nanopatterning was performed on both 8-monolayer (ML) Fe films grown in ultrahigh vacuum as well as 22-ML films stabilized by dosing carbon monoxide during growth. The structural transformation of these nano-patterned films was investigated using scanning tunneling microscopy. In both 8 and 22-ML fcc Fe films, the bcc needles are found to protrude laterally out of the irradiated part of the sample, limiting the resolution of the technique to a few 10 nm. The magnetic transformation was confirmed by magnetic force microscopy.

Název v anglickém jazyce

In-situ magnetic nano-patterning of Fe films grown on Cu(100)

Popis výsledku anglicky

Metastable paramagnetic face-centered cubic (fcc) Fe films grown on a Cu(100) single crystal at room temperature can be transformed to the ferromagnetic body-centered cubic (bcc) structure by ion irradiation. We have employed this technique to write small ferromagnetic patches by Ar irradiation through a gold coated SiN mask with regularly arranged 80-nm diameter holes, which as placed on top of the as-prepared fcc Fe films. Nanopatterning was performed on both 8-monolayer (ML) Fe films grown in ultrahigh vacuum as well as 22-ML films stabilized by dosing carbon monoxide during growth. The structural transformation of these nano-patterned films was investigated using scanning tunneling microscopy. In both 8 and 22-ML fcc Fe films, the bcc needles are found to protrude laterally out of the irradiated part of the sample, limiting the resolution of the technique to a few 10 nm. The magnetic transformation was confirmed by magnetic force microscopy.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BM - Fyzika pevných látek a magnetismus

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Aplied Physics

ISSN

0021-8979

e-ISSN

—

Svazek periodika

110

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

6

Strana od-do

"024309-1"-"024309-6"

Kód UT WoS článku

000293476300091

EID výsledku v databázi Scopus

—