3D Atomistic Simulation of Fatigue Behaviour of Cracked Single Crystal of bcc Iron Loaded in Mode III

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F11%3APU95870" target="_blank" >RIV/00216305:26210/11:PU95870 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/61388998:_____/11:00363795

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

3D Atomistic Simulation of Fatigue Behaviour of Cracked Single Crystal of bcc Iron Loaded in Mode III

Popis výsledku v původním jazyce

We present new results of 3D molecular dynamic (MD) simulations of a mechanical behaviour of an edge crack <110>[110] (crack plane/crack front) in a single crystal of bcc iron cyclically loaded in mode III at room temperature. Our previous 3D molecular dynamic simulations showed that this crack under monotonic uniaxial tension loading in mode I emitted blunting dislocations in the inclined <111>(112) slip systems and it was stable up to very high loads, in qualitative agreement with experiments and continuum predictions. Our question is how the cyclic loading in mode III changes the crack behaviour and its stability. The paper also brings information on how the distribution of external forces in mode III influences the fatigue crack behaviour and how the defects generated by the crack can produce experimentally observed advances of the crack front in local modes I, II, I + II and II + III.

Název v anglickém jazyce

3D Atomistic Simulation of Fatigue Behaviour of Cracked Single Crystal of bcc Iron Loaded in Mode III

Popis výsledku anglicky

We present new results of 3D molecular dynamic (MD) simulations of a mechanical behaviour of an edge crack <110>[110] (crack plane/crack front) in a single crystal of bcc iron cyclically loaded in mode III at room temperature. Our previous 3D molecular dynamic simulations showed that this crack under monotonic uniaxial tension loading in mode I emitted blunting dislocations in the inclined <111>(112) slip systems and it was stable up to very high loads, in qualitative agreement with experiments and continuum predictions. Our question is how the cyclic loading in mode III changes the crack behaviour and its stability. The paper also brings information on how the distribution of external forces in mode III influences the fatigue crack behaviour and how the defects generated by the crack can produce experimentally observed advances of the crack front in local modes I, II, I + II and II + III.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP108%2F10%2F0698" target="_blank" >GAP108/10/0698: Nové přístupy k výzkumu únavového šíření trhliny v módech II, III a II+III</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

INTERNATIONAL JOURNAL OF FATIGUE

ISSN

0142-1123

e-ISSN

—

Svazek periodika

33

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

10

Strana od-do

1564-1573

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—