3D Atomistic Simulation of Fatigue Behavior of a Ductile Crack in BCC Iron loaded in mode II
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F12%3APU96859" target="_blank" >RIV/00216305:26210/12:PU96859 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/61388998:_____/12:00376703
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
3D Atomistic Simulation of Fatigue Behavior of a Ductile Crack in BCC Iron loaded in mode II
Popis výsledku v původním jazyce
We present new results of 3D molecular dynamic (MD) simulations of a mechanical response of an edge crack [110] (crack plane/crack front) in a single crystal of bcc iron cyclically loaded in mode II at room temperature and 0 K under different boundary conditions. Our previous 3D molecular dynamic simulations showed that this crack under monotonic uniaxial tension loading in mode I emitted blunting dislocations in the inclined slip systems and it was stable up to very high loads, in qualitative agreementwith experiments and continuum predictions. Our question is how the cyclic loading in mode II changes the crack behaviour and its stability. The paper also brings information on comparison with fatigue behaviour of the crack loaded in mode I and in modeIII.
Název v anglickém jazyce
3D Atomistic Simulation of Fatigue Behavior of a Ductile Crack in BCC Iron loaded in mode II
Popis výsledku anglicky
We present new results of 3D molecular dynamic (MD) simulations of a mechanical response of an edge crack [110] (crack plane/crack front) in a single crystal of bcc iron cyclically loaded in mode II at room temperature and 0 K under different boundary conditions. Our previous 3D molecular dynamic simulations showed that this crack under monotonic uniaxial tension loading in mode I emitted blunting dislocations in the inclined slip systems and it was stable up to very high loads, in qualitative agreementwith experiments and continuum predictions. Our question is how the cyclic loading in mode II changes the crack behaviour and its stability. The paper also brings information on comparison with fatigue behaviour of the crack loaded in mode I and in modeIII.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GAP108%2F10%2F0698" target="_blank" >GAP108/10/0698: Nové přístupy k výzkumu únavového šíření trhliny v módech II, III a II+III</a><br>
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
COMPUTATIONAL MATERIALS SCIENCE
ISSN
0927-0256
e-ISSN
—
Svazek periodika
61
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
8
Strana od-do
12-19
Kód UT WoS článku
000304562000003
EID výsledku v databázi Scopus
—