Influence of Metallic Dopants on Fracture Behaviour of TiB2 Based Cermets

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F12%3APU104727" target="_blank" >RIV/00216305:26210/12:PU104727 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of Metallic Dopants on Fracture Behaviour of TiB2 Based Cermets

Popis výsledku v původním jazyce

Titanium diboride (TiB2) - metal composites were prepared by hot-pressing of the TiB2 - Ni and Ta doped TiB2-Ni powders. The obvious limitation of pure TiB2 is the bad sinterability, exaggerated grain growth at temperatures exceeded 2000 C needed for thedensification and brittleness. There is only limited number of approaches how to improve fracture resistance. The method used in this work is based on doping the basic microstructure by above mentioned metals. The positive influence of dopants on the microstructure and fracture behaviour was demonstrated by means of mechanical properties and fractographic analysis. The right selection of dopants led to the refinement of microstructure resulted in the increase of flexural strength up to the level of 700MPa and fracture toughness of 5.0 MPa.m1/2.

Název v anglickém jazyce

Influence of Metallic Dopants on Fracture Behaviour of TiB2 Based Cermets

Popis výsledku anglicky

Titanium diboride (TiB2) - metal composites were prepared by hot-pressing of the TiB2 - Ni and Ta doped TiB2-Ni powders. The obvious limitation of pure TiB2 is the bad sinterability, exaggerated grain growth at temperatures exceeded 2000 C needed for thedensification and brittleness. There is only limited number of approaches how to improve fracture resistance. The method used in this work is based on doping the basic microstructure by above mentioned metals. The positive influence of dopants on the microstructure and fracture behaviour was demonstrated by means of mechanical properties and fractographic analysis. The right selection of dopants led to the refinement of microstructure resulted in the increase of flexural strength up to the level of 700MPa and fracture toughness of 5.0 MPa.m1/2.

Druh

D - Stať ve sborníku

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

<a href="/cs/project/ED1.1.00%2F02.0068" target="_blank" >ED1.1.00/02.0068: CEITEC - central european institute of technology</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Acta Metallurgica Slovaca

ISBN

—

ISSN

1335-1532

e-ISSN

—

Počet stran výsledku

8

Strana od-do

98-105

Název nakladatele

Neuveden

Místo vydání

Neuveden

Místo konání akce

Stará Lesná

Datum konání akce

21. 10. 2012

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—