Influence of metallic dopants on fracture behaviour of TiB2 based cermets

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F13%3A00421219" target="_blank" >RIV/68081723:_____/13:00421219 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.12776/amsc.v3i0.112" target="_blank" >http://dx.doi.org/10.12776/amsc.v3i0.112</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.12776/amsc.v3i0.112" target="_blank" >10.12776/amsc.v3i0.112</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of metallic dopants on fracture behaviour of TiB2 based cermets

Popis výsledku v původním jazyce

Titanium diboride (TiB2) - metal composites were prepared by hot-pressing of the TiB2 - Ni and Ta doped TiB2-Ni powders. The obvious limitation of pure TiB2 is the bad sinterability, exaggerated grain growth at temperatures exceeded 2000°C needed for thedensification and brittleness. There is only limited number of approaches how to improve fracture resistance. The method used in this work is based on doping the basic microstructure by above mentioned metals. The positive influence of dopants on the microstructure and fracture behaviour was demonstrated by means of mechanical properties and fractographic analysis. The right selection of dopants led to the refinement of microstructure resulted in the increase of flexural strength up to the level of 700MPa and fracture toughness of 5.0 MPa.m1/2.

Název v anglickém jazyce

Influence of metallic dopants on fracture behaviour of TiB2 based cermets

Popis výsledku anglicky

Titanium diboride (TiB2) - metal composites were prepared by hot-pressing of the TiB2 - Ni and Ta doped TiB2-Ni powders. The obvious limitation of pure TiB2 is the bad sinterability, exaggerated grain growth at temperatures exceeded 2000°C needed for thedensification and brittleness. There is only limited number of approaches how to improve fracture resistance. The method used in this work is based on doping the basic microstructure by above mentioned metals. The positive influence of dopants on the microstructure and fracture behaviour was demonstrated by means of mechanical properties and fractographic analysis. The right selection of dopants led to the refinement of microstructure resulted in the increase of flexural strength up to the level of 700MPa and fracture toughness of 5.0 MPa.m1/2.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Acta Metallurgica Slovaca Conference

ISSN

1338-1660

e-ISSN

—

Svazek periodika

3

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

8

Strana od-do

98-105

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—