Study of cyclic strain localization and fatigue crack initiation using FIB technique

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F12%3APU93040" target="_blank" >RIV/00216305:26210/12:PU93040 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68081723:_____/12:00385355

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Study of cyclic strain localization and fatigue crack initiation using FIB technique

Popis výsledku v původním jazyce

Focused ion beam (FIB) technique together with other advanced microscopic techniques was applied to study the early microstructural changes leading to fatigue crack initiation in cyclically strained polycrystals (nickel, 316L steel). Dislocation structures of persistent slip bands (PSBs) and surrounding matrix were investigated in detail using electron channeling contrast imaging (ECCI) technique (concurrently in the FIB cross-section and on the specimen surface) and simultaneously with the surface relief topography using transmission electron microscopy (TEM) of thin surface foils prepared by in situ lift-out technique. True shape of extrusions and intrusions and the path of initiated fatigue cracks were assessed in three dimensions by FIB micro-tomography. The role of twin boundary in cyclic strain localization and fatigue crack initiation is discussed. Principal advantages and some limitations of FIB technique in fatigue crack initiation studies in polycrystals are highlighted.

Název v anglickém jazyce

Study of cyclic strain localization and fatigue crack initiation using FIB technique

Popis výsledku anglicky

Focused ion beam (FIB) technique together with other advanced microscopic techniques was applied to study the early microstructural changes leading to fatigue crack initiation in cyclically strained polycrystals (nickel, 316L steel). Dislocation structures of persistent slip bands (PSBs) and surrounding matrix were investigated in detail using electron channeling contrast imaging (ECCI) technique (concurrently in the FIB cross-section and on the specimen surface) and simultaneously with the surface relief topography using transmission electron microscopy (TEM) of thin surface foils prepared by in situ lift-out technique. True shape of extrusions and intrusions and the path of initiated fatigue cracks were assessed in three dimensions by FIB micro-tomography. The role of twin boundary in cyclic strain localization and fatigue crack initiation is discussed. Principal advantages and some limitations of FIB technique in fatigue crack initiation studies in polycrystals are highlighted.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP108%2F10%2F2371" target="_blank" >GAP108/10/2371: Lokalizace a ireverzibilita cyklického skluzu v polykrystalech</a><br>

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

INTERNATIONAL JOURNAL OF FATIGUE

ISSN

0142-1123

e-ISSN

—

Svazek periodika

39

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

8

Strana od-do

44-53

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—