Application of FIB technique to study of early fatigue damage in polycrystals
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F10%3A00353531" target="_blank" >RIV/68081723:_____/10:00353531 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216305:26210/10:PU87809
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Application of FIB technique to study of early fatigue damage in polycrystals
Popis výsledku v původním jazyce
Focused ion beam (FIB) technique together with other advanced microscopic techniques were applied to study early microstructural changes leading to crack initiation in fatigued polycrystals. Dislocation structures of persistent slip bands (PSBs) and surrounding matrix were revealed in the bulk of surface grains by electron channelling contrast imaging (ECCI) technique on the FIB cross-sections. True shape of extrusions, intrusions and the path of initiated fatigue cracks were assessed in three dimensions by serial FIB cross-sectioning (FIB tomography). Advantageous potential of FIB technique and its other possible utilization in fatigue crack initiation studies in polycrystals are highlighted.
Název v anglickém jazyce
Application of FIB technique to study of early fatigue damage in polycrystals
Popis výsledku anglicky
Focused ion beam (FIB) technique together with other advanced microscopic techniques were applied to study early microstructural changes leading to crack initiation in fatigued polycrystals. Dislocation structures of persistent slip bands (PSBs) and surrounding matrix were revealed in the bulk of surface grains by electron channelling contrast imaging (ECCI) technique on the FIB cross-sections. True shape of extrusions, intrusions and the path of initiated fatigue cracks were assessed in three dimensions by serial FIB cross-sectioning (FIB tomography). Advantageous potential of FIB technique and its other possible utilization in fatigue crack initiation studies in polycrystals are highlighted.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Physics: Conference Series
ISSN
1742-6588
e-ISSN
—
Svazek periodika
240
Číslo periodika v rámci svazku
-
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
4
Strana od-do
—
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—