MULTICOMPONENT ALLOY POWDERS PREPARATION BY MECHANICAL ALLOYING

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F15%3APU114886" target="_blank" >RIV/00216305:26210/15:PU114886 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

MULTICOMPONENT ALLOY POWDERS PREPARATION BY MECHANICAL ALLOYING

Popis výsledku v původním jazyce

In the last decade, multicomponent alloys arisen as new promising family of materials. The effect of milling parameters, namely milling balls size, milling speed and time on synthesis of inequiatomic AlCoCrFeNiTi0,5 mechanically alloyed (MA) powders in planetary ball mill were studied. Alloying behaviour, morphology, size and homogeneity of powders were observed by X-ray diffraction (XRD) and scanning electron microscopy (SEM). During MA, a supersaturated Cr based solid solution with BCC structure was formed after 24 hours of milling, with significantly reduced grain size. It was revealed, that selection of milling conditions have a great influence on milled powders properties. In general softer milling condition result in decreased particle size and homogeneity

Název v anglickém jazyce

MULTICOMPONENT ALLOY POWDERS PREPARATION BY MECHANICAL ALLOYING

Popis výsledku anglicky

In the last decade, multicomponent alloys arisen as new promising family of materials. The effect of milling parameters, namely milling balls size, milling speed and time on synthesis of inequiatomic AlCoCrFeNiTi0,5 mechanically alloyed (MA) powders in planetary ball mill were studied. Alloying behaviour, morphology, size and homogeneity of powders were observed by X-ray diffraction (XRD) and scanning electron microscopy (SEM). During MA, a supersaturated Cr based solid solution with BCC structure was formed after 24 hours of milling, with significantly reduced grain size. It was revealed, that selection of milling conditions have a great influence on milled powders properties. In general softer milling condition result in decreased particle size and homogeneity

Druh

D - Stať ve sborníku

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2015

ISBN

978-80-87294-62-8

ISSN

—

e-ISSN

—

Počet stran výsledku

300

Strana od-do

195-205

Název nakladatele

TANGER Ltd.

Místo vydání

Brno

Místo konání akce

Brno

Datum konání akce

3. 6. 2015

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000374706100258