Understanding the edge crack phenomenon in ceramic laminates

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F15%3APU115446" target="_blank" >RIV/00216305:26210/15:PU115446 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.fracturae.com/index.php/fis/article/view/IGF-ESIS.34.40" target="_blank" >http://www.fracturae.com/index.php/fis/article/view/IGF-ESIS.34.40</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3221/IGF-ESIS.34.40" target="_blank" >10.3221/IGF-ESIS.34.40</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Understanding the edge crack phenomenon in ceramic laminates

Popis výsledku v původním jazyce

In this work, a 2D parametric finite element model has been developed to predict the onset and propagation of an edge crack in ceramic laminates using a coupled stress-energy criterion. This approach states that a crack is originated when both stress and energy criteria are fulfilled simultaneously. Several designs with different residual stresses and a given thickness in the compressive layers have been computed. The results predict the existence of a lower bound, below no edge crack will be observed, and an upper bound, beyond which the onset of an edge crack would lead to the complete fracture of the layer.

Název v anglickém jazyce

Understanding the edge crack phenomenon in ceramic laminates

Popis výsledku anglicky

In this work, a 2D parametric finite element model has been developed to predict the onset and propagation of an edge crack in ceramic laminates using a coupled stress-energy criterion. This approach states that a crack is originated when both stress and energy criteria are fulfilled simultaneously. Several designs with different residual stresses and a given thickness in the compressive layers have been computed. The results predict the existence of a lower bound, below no edge crack will be observed, and an upper bound, beyond which the onset of an edge crack would lead to the complete fracture of the layer.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20504 - Ceramics

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Frattura ed Integrita Strutturale

ISSN

1971-8993

e-ISSN

—

Svazek periodika

9

Číslo periodika v rámci svazku

34

Stát vydavatele periodika

IT - Italská republika

Počet stran výsledku

9

Strana od-do

362-370

Kód UT WoS článku

000385961800040

EID výsledku v databázi Scopus

2-s2.0-84942760300