Modelling of edge crack formation and propagation in ceramic laminates using the stress–energy coupled criterion

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F16%3APU120793" target="_blank" >RIV/00216305:26210/16:PU120793 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.sciencedirect.com/science/article/pii/S001379441630145X" target="_blank" >http://www.sciencedirect.com/science/article/pii/S001379441630145X</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.engfracmech.2016.03.039" target="_blank" >10.1016/j.engfracmech.2016.03.039</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Modelling of edge crack formation and propagation in ceramic laminates using the stress–energy coupled criterion

Popis výsledku v původním jazyce

The high compressive stresses in ceramic laminates utilized to enhance their fracture resistance may lead to the formation of edge cracks at the surface of the compressive layers. In this work, a 2D parametric numerical model is developed to assess the effect of residual stress and thickness of the compressive layers on the edge crack formation, by using a coupled stress–energy criterion. The results predict the existence of a lower bound, below which no edge crack occurs (i.e. obtaining crack-free laminates), and an upper bound, beyond which onset of the edge crack would lead to the complete delamination of the compressive layer.

Název v anglickém jazyce

Modelling of edge crack formation and propagation in ceramic laminates using the stress–energy coupled criterion

Popis výsledku anglicky

The high compressive stresses in ceramic laminates utilized to enhance their fracture resistance may lead to the formation of edge cracks at the surface of the compressive layers. In this work, a 2D parametric numerical model is developed to assess the effect of residual stress and thickness of the compressive layers on the edge crack formation, by using a coupled stress–energy criterion. The results predict the existence of a lower bound, below which no edge crack occurs (i.e. obtaining crack-free laminates), and an upper bound, beyond which onset of the edge crack would lead to the complete delamination of the compressive layer.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20504 - Ceramics

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Engineering Fracture Mechanics

ISSN

0013-7944

e-ISSN

1873-7315

Svazek periodika

167

Číslo periodika v rámci svazku

2016

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

11

Strana od-do

45-55

Kód UT WoS článku

000387329000005

EID výsledku v databázi Scopus

2-s2.0-84964325926