Mechanical properties and microstructure of Al-Cu alloy processed by SLM

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F15%3APU117133" target="_blank" >RIV/00216305:26210/15:PU117133 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Mechanical properties and microstructure of Al-Cu alloy processed by SLM

Popis výsledku v původním jazyce

Paper deal with comparison of mechanical properties and microstructure of aluminium alloy EN AW 2618A prepared using Selective Laser Melting (SLM) process and of material of the same grade processed by extrusion. It was found that defects present in microstructure of SLM material significantly affect its mechanical properties. when 0.2% proof stress was 191 MPa, UTS was 208 MPa and elongation at the break was 0.6 %, whereas measured values for extruded state were substantially higher: 0,2% proof stresswas 273 MPa, UTS = 392 MPa, elongation at the break = 13.7 %.

Název v anglickém jazyce

Mechanical properties and microstructure of Al-Cu alloy processed by SLM

Popis výsledku anglicky

Paper deal with comparison of mechanical properties and microstructure of aluminium alloy EN AW 2618A prepared using Selective Laser Melting (SLM) process and of material of the same grade processed by extrusion. It was found that defects present in microstructure of SLM material significantly affect its mechanical properties. when 0.2% proof stress was 191 MPa, UTS was 208 MPa and elongation at the break was 0.6 %, whereas measured values for extruded state were substantially higher: 0,2% proof stresswas 273 MPa, UTS = 392 MPa, elongation at the break = 13.7 %.

Druh

O - Ostatní výsledky

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů