Fracture behaviour of weld joints made of pearlitic and bainitic steel

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F16%3APU119402" target="_blank" >RIV/00216305:26210/16:PU119402 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Fracture behaviour of weld joints made of pearlitic and bainitic steel

Popis výsledku v původním jazyce

The paper is concerned with microstructure evaluations and the hardness and fracture behaviour of welded joints made from cast bainitic Lo8CrNiMo steel and pearlitic rail steel of the type UIC 900A. The materials mentioned are predetermined for frogs of switches. The study is based mainly on microstructural observations and hardness measurements of the base materials, weld, and heat affected zone (HAZ). Dynamic fracture toughness was evaluated based on data from pre-cracked Charpy type specimens. The pearlitic UIC 900A steel and its HAZ had the lowest dynamic fracture toughness values and therefore the highest risk of brittle fracture. At application temperature range, this steel is on the lower shelf of the ductile-to-brittle transition, and the tempering in the HAZ did not affect the toughness substantially. The cast bainitic steel in the weld joint is characterized by higher toughness values compared to the pearlitic one, and a further increase in toughness may be expected in the HAZ. The weld zone itself is characterized by high scatter of toughness data; nevertheless, all the values are above the scatter band characterizing the pearlitic steel.

Název v anglickém jazyce

Fracture behaviour of weld joints made of pearlitic and bainitic steel

Popis výsledku anglicky

The paper is concerned with microstructure evaluations and the hardness and fracture behaviour of welded joints made from cast bainitic Lo8CrNiMo steel and pearlitic rail steel of the type UIC 900A. The materials mentioned are predetermined for frogs of switches. The study is based mainly on microstructural observations and hardness measurements of the base materials, weld, and heat affected zone (HAZ). Dynamic fracture toughness was evaluated based on data from pre-cracked Charpy type specimens. The pearlitic UIC 900A steel and its HAZ had the lowest dynamic fracture toughness values and therefore the highest risk of brittle fracture. At application temperature range, this steel is on the lower shelf of the ductile-to-brittle transition, and the tempering in the HAZ did not affect the toughness substantially. The cast bainitic steel in the weld joint is characterized by higher toughness values compared to the pearlitic one, and a further increase in toughness may be expected in the HAZ. The weld zone itself is characterized by high scatter of toughness data; nevertheless, all the values are above the scatter band characterizing the pearlitic steel.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/LO1202" target="_blank" >LO1202: NETME CENTRE PLUS</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materiálové inžinierstvo

ISSN

1335-0803

e-ISSN

—

Svazek periodika

23

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

10

Strana od-do

33-42

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—