Interaction of Creep and High Cycle Fatigue of IN 713LC Superalloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F17%3APU120001" target="_blank" >RIV/00216305:26210/17:PU120001 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.scopus.com/record/display.uri?eid=2-s2.0-85009830512&origin=resultslist&sort=plf-f&src=s&st1=Interaction+of+Creep+and+High+Cycle+Fatigue+of+IN+713LC+Superalloy&st2=&sid=5A0FE1F1FC3C8966B2D306799B19A00D.wsnAw8kcdt7IPYLO0V48gA%3a10&sot=b&sdt=b&" target="_blank" >https://www.scopus.com/record/display.uri?eid=2-s2.0-85009830512&origin=resultslist&sort=plf-f&src=s&st1=Interaction+of+Creep+and+High+Cycle+Fatigue+of+IN+713LC+Superalloy&st2=&sid=5A0FE1F1FC3C8966B2D306799B19A00D.wsnAw8kcdt7IPYLO0V48gA%3a10&sot=b&sdt=b&</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/www.scientific.net/SSP.258.595" target="_blank" >10.4028/www.scientific.net/SSP.258.595</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Interaction of Creep and High Cycle Fatigue of IN 713LC Superalloy

Popis výsledku v původním jazyce

The study deals with the interaction of creep and high cycle fatigue of cast polycrystalline nickel-based superalloy IN 713LC at high temperatures. Previous works indicated that creep lifetime of superalloy structures was un-affected or even slightly increased in the cases with superimposed vibrations. The reason for this behaviour was not well described up to now. Therefore, set of fatigue tests was conducted at high mean stresses level to observe this phenomenon. The mean stress was kept constant while the stress amplitudes were selected in order to measure wide range of conditions from pure creep to pure fatigue. Fractographic analysis by scanning electron microscopy (SEM) was done with the aim to identify governing damage mechanisms for particular test conditions as a preliminary evaluation of conducted tests.

Název v anglickém jazyce

Interaction of Creep and High Cycle Fatigue of IN 713LC Superalloy

Popis výsledku anglicky

The study deals with the interaction of creep and high cycle fatigue of cast polycrystalline nickel-based superalloy IN 713LC at high temperatures. Previous works indicated that creep lifetime of superalloy structures was un-affected or even slightly increased in the cases with superimposed vibrations. The reason for this behaviour was not well described up to now. Therefore, set of fatigue tests was conducted at high mean stresses level to observe this phenomenon. The mean stress was kept constant while the stress amplitudes were selected in order to measure wide range of conditions from pure creep to pure fatigue. Fractographic analysis by scanning electron microscopy (SEM) was done with the aim to identify governing damage mechanisms for particular test conditions as a preliminary evaluation of conducted tests.

Druh

J_SC - Článek v periodiku v databázi SCOPUS

CEP obor

—

OECD FORD obor

20306 - Audio engineering, reliability analysis

Projekt

<a href="/cs/project/LO1202" target="_blank" >LO1202: NETME CENTRE PLUS</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Solid State Phenomena

ISSN

1012-0394

e-ISSN

—

Svazek periodika

258

Číslo periodika v rámci svazku

2017

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

4

Strana od-do

595-598

Kód UT WoS článku

—

EID výsledku v databázi Scopus

2-s2.0-85009830512