Interaction of fatigue and creep in MAR-M 247 superalloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F20%3APU136695" target="_blank" >RIV/00216305:26210/20:PU136695 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.sciencedirect.com/science/article/pii/S2452321620301451" target="_blank" >https://www.sciencedirect.com/science/article/pii/S2452321620301451</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.prostr.2020.01.086" target="_blank" >10.1016/j.prostr.2020.01.086</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Interaction of fatigue and creep in MAR-M 247 superalloy

Popis výsledku v původním jazyce

Lifetime of MAR-M 247 Ni-based superalloy was experimentally studied under high-frequency cyclic loading (120 Hz) with constant tensile mean stress σm = 300 MPa at temperature 900 °C in air. The stress amplitude σa was changed in order to investigate the superalloy lifetime in a wide range of conditions, from pure creep to pure fatigue. The superposition of the stress amplitude on the mean stress does not influence the specimen lifetime until a threshold value is reached. Scanning electron microscopy was utilized for the fracture surface observation with the aim to identify the governing damage mechanisms for particular test conditions.

Název v anglickém jazyce

Interaction of fatigue and creep in MAR-M 247 superalloy

Popis výsledku anglicky

Lifetime of MAR-M 247 Ni-based superalloy was experimentally studied under high-frequency cyclic loading (120 Hz) with constant tensile mean stress σm = 300 MPa at temperature 900 °C in air. The stress amplitude σa was changed in order to investigate the superalloy lifetime in a wide range of conditions, from pure creep to pure fatigue. The superposition of the stress amplitude on the mean stress does not influence the specimen lifetime until a threshold value is reached. Scanning electron microscopy was utilized for the fracture surface observation with the aim to identify the governing damage mechanisms for particular test conditions.

Druh

J_SC - Článek v periodiku v databázi SCOPUS

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/EF16_025%2F0007304" target="_blank" >EF16_025/0007304: Materiály s vnitřní architekturou strukturované pro aditivní technologie</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2020

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Procedia Structural Integrity

ISSN

2452-3216

e-ISSN

—

Svazek periodika

23

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

IT - Italská republika

Počet stran výsledku

6

Strana od-do

197-202

Kód UT WoS článku

—

EID výsledku v databázi Scopus

2-s2.0-85094204013