Possibility for improving damage tolerance of integral structure by high strength bonded straps

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26210%2F17%3APU123775" target="_blank" >RIV/00216305:26210/17:PU123775 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Possibility for improving damage tolerance of integral structure by high strength bonded straps

Popis výsledku v původním jazyce

Integral stringer panels can attain weight reduction in a primary aircraft structures, but does not contain physical barriers for fatigue crack growth. One of the promising technique for prolonging fatigue life are bonded crack retarders made of materials with high stiffness. Experimental study was done on two specimens with different geometries. The straps consisted of high strength corrosion resistant steel AISI 301 was adhesively bonded to an aluminium alloy 2024-T351 Center-Cracked Tension (CCT) specimens fabricated by a high-speed machining process to promote fatigue crack growth retardation. Specimens were tested at constant amplitude load. The study concludes that the fatigue crack growth life can be significantly improved.

Název v anglickém jazyce

Possibility for improving damage tolerance of integral structure by high strength bonded straps

Popis výsledku anglicky

Integral stringer panels can attain weight reduction in a primary aircraft structures, but does not contain physical barriers for fatigue crack growth. One of the promising technique for prolonging fatigue life are bonded crack retarders made of materials with high stiffness. Experimental study was done on two specimens with different geometries. The straps consisted of high strength corrosion resistant steel AISI 301 was adhesively bonded to an aluminium alloy 2024-T351 Center-Cracked Tension (CCT) specimens fabricated by a high-speed machining process to promote fatigue crack growth retardation. Specimens were tested at constant amplitude load. The study concludes that the fatigue crack growth life can be significantly improved.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20304 - Aerospace engineering

Projekt

<a href="/cs/project/TE02000032" target="_blank" >TE02000032: Výzkumné centrum pokročilých leteckých konstrukcí</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

14th Seminar "Materials and technologies in Special Technics Production 2017"

ISBN

978-80-7231-420-1

ISSN

—

e-ISSN

—

Počet stran výsledku

5

Strana od-do

29-33

Název nakladatele

University of Defence

Místo vydání

Brno

Místo konání akce

Brno

Datum konání akce

1. 6. 2017

Typ akce podle státní příslušnosti

CST - Celostátní akce

Kód UT WoS článku

—