Heat Treatment of the SLM Processed Lattice Structure Made of AlSi10Mg and Its Effect on the Impact Energy Absorption

Kód výsledku v IS VaVaI

RIV/00216305:26210/19:PU133741 - isvavai.cz

Výsledek na webu

https://www.europm2019.com/

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Heat Treatment of the SLM Processed Lattice Structure Made of AlSi10Mg and Its Effect on the Impact Energy Absorption

Popis výsledku v původním jazyce

This paper deals with the heat treatment effect on the deformation behaviour of AlSi10Mg lattice structures under impact loading. As the sample, lattice structure cubes (20×20×20 mm) covered with thin plates were used. The effect of simple annealing and solution treatment with water quenching and artificial ageing were compared. The results showed a positive effect of annealing on the deformation behaviour compared with the as-built state. Due to heat treatment, the elongation of the lattice structure raised, the deformation behaviour was stabilized, and the cumulative absorbed energy was similar as is the as-built state with higher energy absorption efficiency.

Název v anglickém jazyce

Heat Treatment of the SLM Processed Lattice Structure Made of AlSi10Mg and Its Effect on the Impact Energy Absorption

Popis výsledku anglicky

This paper deals with the heat treatment effect on the deformation behaviour of AlSi10Mg lattice structures under impact loading. As the sample, lattice structure cubes (20×20×20 mm) covered with thin plates were used. The effect of simple annealing and solution treatment with water quenching and artificial ageing were compared. The results showed a positive effect of annealing on the deformation behaviour compared with the as-built state. Due to heat treatment, the elongation of the lattice structure raised, the deformation behaviour was stabilized, and the cumulative absorbed energy was similar as is the as-built state with higher energy absorption efficiency.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

EF16_025/0007304: Materiály s vnitřní architekturou strukturované pro aditivní technologie

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Euro PM2019 Proceedings

ISBN

978-1-899072-51-4

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

1-6

Název nakladatele

Neuveden

Místo vydání

Maastricht

Místo konání akce

Maastricht

Datum konání akce

13. 10. 2019

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—