The Spread of Corrosion of the Deposited Material Using the Cold Spray Method

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26220%2F21%3APU142768" target="_blank" >RIV/00216305:26220/21:PU142768 - isvavai.cz</a>
Výsledek na webu
<a href="https://iopscience.iop.org/article/10.1149/10501.0355ecst" target="_blank" >https://iopscience.iop.org/article/10.1149/10501.0355ecst</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1149/10501.0355ecst" target="_blank" >10.1149/10501.0355ecst</a>

Jazyk výsledku
angličtina
Název v původním jazyce
The Spread of Corrosion of the Deposited Material Using the Cold Spray Method
Popis výsledku v původním jazyce
A layer of copper was applied to the base aluminum material using the cold spray method (cold kinetic deposition). The samples were exposed to corrosion in a salt chamber for 100, 200 and 300 hours. The change in the size of the internal and surface resistance of the samples was monitored. The corrosion results were also examined using an electron microscope.
Název v anglickém jazyce
The Spread of Corrosion of the Deposited Material Using the Cold Spray Method
Popis výsledku anglicky
A layer of copper was applied to the base aluminum material using the cold spray method (cold kinetic deposition). The samples were exposed to corrosion in a salt chamber for 100, 200 and 300 hours. The change in the size of the internal and surface resistance of the samples was monitored. The corrosion results were also examined using an electron microscope.