The kinetics of Al-Si spinel phase crystallization from calcined kaolin
Popis výsledku v původním jazyce
The crystallization of Al-Si spinel from medium ordered kaolin with high content of kaolinite was investigated using the differential thermal analysis (DTA). The apparent activation energy of the process was evaluated from the dependence of exothermic peak of crystallization on heating rate. Within the applied interval of heating rate (1-40 K min-1) the temperature of peak maximum increases from initial value of 1220.5 K in about 54.2 K. The apparent activation energy of the process 856 +/- 2 kJ mol-1was calculated using the Kissinger equation. The growth morphology of Al-Si spinel crystal was evaluated from the Avrami parameter. The average value of morphology parameter determined within the observed interval of heating rate is 3.08 +/- 0.03. This value indicates that crystallization mechanism of Al-Si spinel phase proceeds by bulk nucleation of the new phase with constant number of nuclei and that the three-dimensional growth of crystals is controlled by the reaction rate on the phas
Název v anglickém jazyce
The kinetics of Al-Si spinel phase crystallization from calcined kaolin
Popis výsledku anglicky
The crystallization of Al-Si spinel from medium ordered kaolin with high content of kaolinite was investigated using the differential thermal analysis (DTA). The apparent activation energy of the process was evaluated from the dependence of exothermic peak of crystallization on heating rate. Within the applied interval of heating rate (1-40 K min-1) the temperature of peak maximum increases from initial value of 1220.5 K in about 54.2 K. The apparent activation energy of the process 856 +/- 2 kJ mol-1was calculated using the Kissinger equation. The growth morphology of Al-Si spinel crystal was evaluated from the Avrami parameter. The average value of morphology parameter determined within the observed interval of heating rate is 3.08 +/- 0.03. This value indicates that crystallization mechanism of Al-Si spinel phase proceeds by bulk nucleation of the new phase with constant number of nuclei and that the three-dimensional growth of crystals is controlled by the reaction rate on the phas
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CA - Anorganická chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>O - Projekt operacniho programu
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
JOURNAL OF SOLID STATE CHEMISTRY
ISSN
0022-4596
e-ISSN
—
Svazek periodika
183
Číslo periodika v rámci svazku
11
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
5
Strana od-do
—
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—