Non-isothermal Kinetic Analysis of Processes Occurring During Thermal Treatment of Kaolinite
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F17%3A00312610" target="_blank" >RIV/68407700:21110/17:00312610 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1063/1.4994508" target="_blank" >http://dx.doi.org/10.1063/1.4994508</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1063/1.4994508" target="_blank" >10.1063/1.4994508</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Non-isothermal Kinetic Analysis of Processes Occurring During Thermal Treatment of Kaolinite
Popis výsledku v původním jazyce
A non-isothermal kinetic analysis of processes occurring during thermal treatment of kaolinite is carried out using differential thermal analysis on powder samples with heating rates from 1 to 10 °C min–1 in static air atmosphere. For the parameterization of dehydroxylation process and crystallization of Al-Si spinel phase from metakaolinite the Kissinger method is used. The determined values of apparent activation energy for the dehydroxylation of kaolinite and formation of Al-Si spinel phase are (163 ± 11) kJ mol–1 and (826 ± 16) kJ mol–1, respectively. For the dehydroxylation of kaolinite the diffusion controlled growth of a new phase with a decreasing nucleation rate is determined as a mechanism of the process. The results also show that the formation of Al-Si spinel phase from metakaolinite is controlled by grain edge nucleation after saturation.
Název v anglickém jazyce
Non-isothermal Kinetic Analysis of Processes Occurring During Thermal Treatment of Kaolinite
Popis výsledku anglicky
A non-isothermal kinetic analysis of processes occurring during thermal treatment of kaolinite is carried out using differential thermal analysis on powder samples with heating rates from 1 to 10 °C min–1 in static air atmosphere. For the parameterization of dehydroxylation process and crystallization of Al-Si spinel phase from metakaolinite the Kissinger method is used. The determined values of apparent activation energy for the dehydroxylation of kaolinite and formation of Al-Si spinel phase are (163 ± 11) kJ mol–1 and (826 ± 16) kJ mol–1, respectively. For the dehydroxylation of kaolinite the diffusion controlled growth of a new phase with a decreasing nucleation rate is determined as a mechanism of the process. The results also show that the formation of Al-Si spinel phase from metakaolinite is controlled by grain edge nucleation after saturation.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20101 - Civil engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/GBP105%2F12%2FG059" target="_blank" >GBP105/12/G059: Kumulativní časově závislé procesy ve stavebních materiálech a konstrukcích</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
THERMOPHYSICS 2017: 22nd International Meeting of Thermophysics 2017 and 4th Meeting of EnRe 2017
ISBN
978-0-7354-1546-1
ISSN
—
e-ISSN
1551-7616
Počet stran výsledku
5
Strana od-do
—
Název nakladatele
American Institute of Physic AIP
Místo vydání
Santa Fe
Místo konání akce
Těrchová
Datum konání akce
12. 9. 2017
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000426600400033