The synthesis and characterization of an expansive admixture for M-type cements I. The influence of free CaO to the formation of ettringite
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26310%2F12%3APU100886" target="_blank" >RIV/00216305:26310/12:PU100886 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The synthesis and characterization of an expansive admixture for M-type cements I. The influence of free CaO to the formation of ettringite
Popis výsledku v původním jazyce
The hydration process of expansive admixtures for M-type of expansive or shrinkage compensation cements was studied by thermal analysis supplemented by infrared spectroscopy and X-ray diffraction. The main attention was focused on ettringite formation and on the influence of lime content upon the process. The behaviour of expansive admixture during hydration is significantly affected by the content of lime. The increasing content of lime slows down the rate of ettringite formation and supports the formation of monosulphate (AFm phase) that can be transformed afterwards into ettringite during hardening process. This process may produce better expansion effect because of better transfer of expansion stress after the setting of the paste
Název v anglickém jazyce
The synthesis and characterization of an expansive admixture for M-type cements I. The influence of free CaO to the formation of ettringite
Popis výsledku anglicky
The hydration process of expansive admixtures for M-type of expansive or shrinkage compensation cements was studied by thermal analysis supplemented by infrared spectroscopy and X-ray diffraction. The main attention was focused on ettringite formation and on the influence of lime content upon the process. The behaviour of expansive admixture during hydration is significantly affected by the content of lime. The increasing content of lime slows down the rate of ettringite formation and supports the formation of monosulphate (AFm phase) that can be transformed afterwards into ettringite during hardening process. This process may produce better expansion effect because of better transfer of expansion stress after the setting of the paste
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
CA - Anorganická chemie
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/ED0012%2F01%2F01" target="_blank" >ED0012/01/01: Centra materiálového výzkumu na FCH VUT v Brně</a><br>
Návaznosti
O - Projekt operacniho programu
Ostatní
Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Thermal Analysis and Calorimetry
ISSN
1388-6150
e-ISSN
—
Svazek periodika
2012
Číslo periodika v rámci svazku
7
Stát vydavatele periodika
HU - Maďarsko
Počet stran výsledku
10
Strana od-do
1-10
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—