Plasmachemical Removal of Corrosion Layers from Brass

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26310%2F12%3APU99279" target="_blank" >RIV/00216305:26310/12:PU99279 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Plasmachemical Removal of Corrosion Layers from Brass
Popis výsledku v původním jazyce
Influence of RF low-pressure hydrogen plasma on corroded brass samples was investigated. OH radicals formed during this process were measured by optical emission spectroscopy; simultaneously, sample temperature was measured by a thermocouple. The value of integral intensity of OH radicals represented quantitative ablation of oxygen from a corrosion layer. Sample temperature was an important indicator of sample protection against metallographic changes. It was proved that both hydrogen atom reduction andthermal decomposition were employed in the removal process.
Název v anglickém jazyce
Plasmachemical Removal of Corrosion Layers from Brass
Popis výsledku anglicky
Influence of RF low-pressure hydrogen plasma on corroded brass samples was investigated. OH radicals formed during this process were measured by optical emission spectroscopy; simultaneously, sample temperature was measured by a thermocouple. The value of integral intensity of OH radicals represented quantitative ablation of oxygen from a corrosion layer. Sample temperature was an important indicator of sample protection against metallographic changes. It was proved that both hydrogen atom reduction andthermal decomposition were employed in the removal process.

Projekt
<a href="/cs/project/DF11P01OVV004" target="_blank" >DF11P01OVV004: Plazmochemické procesy a technologie pro konzervaci kovových archeologických předmětů</a><br>
Návaznosti
S - Specificky vyzkum na vysokych skolach

Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)