Reduction of Brass Corrosion Layers Using Hydrogen Plasma

Popis výsledku v původním jazyce

Brass corroded model samples were treated in low pressure low temperature hydrogen plasma. Relative intensity of OH radicals and sample temperature were monitored during treatment. Samples were analyzed by XRD pattern. Effects of plasma discharge mean powers were compared in this present article. Relative intensity of OH radicals and temperature were lower during the pulsed regime.

Název v anglickém jazyce

Reduction of Brass Corrosion Layers Using Hydrogen Plasma

Popis výsledku anglicky

Brass corroded model samples were treated in low pressure low temperature hydrogen plasma. Relative intensity of OH radicals and sample temperature were monitored during treatment. Samples were analyzed by XRD pattern. Effects of plasma discharge mean powers were compared in this present article. Relative intensity of OH radicals and temperature were lower during the pulsed regime.

Druh

O - Ostatní výsledky

CEP obor

AC - Archeologie, antropologie, etnologie

OECD FORD obor

—

Projekt

<a href="/cs/project/DF11P01OVV004" target="_blank" >DF11P01OVV004: Plazmochemické procesy a technologie pro konzervaci kovových archeologických předmětů</a><br>

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů