Characterization of the brass threads

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26310%2F13%3APU108323" target="_blank" >RIV/00216305:26310/13:PU108323 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Characterization of the brass threads

Popis výsledku v původním jazyce

The research report has 12 pages. It was prepared for the company IMI International Ltd. Norgren CZ (ordered January 14, 2013). Preparation and measurement of delivered samples is described. The values of maximal sustained torque and designation of samples (provided by client): 1701465 ? 34.8 Nm, 1701466 ? 30.4 Nm, 36336100 ? 56.0 Nm, 36336200 ? 57.9 Nm. The structure of brass samples especially in the threaded section (as required) was observed by the inverted light microscope ZEISS AXIO OBSERVER Z1m.The hardness and microhardness was measured using a LECO microhardness tester AMH43. The structure analysis of fracture surface and element analysis was performed on a scanning electron microscope JEOL JSM-7600F with an energy dispersive analyzer OXFORDX-Max 20 mm2.

Název v anglickém jazyce

Characterization of the brass threads

Popis výsledku anglicky

The research report has 12 pages. It was prepared for the company IMI International Ltd. Norgren CZ (ordered January 14, 2013). Preparation and measurement of delivered samples is described. The values of maximal sustained torque and designation of samples (provided by client): 1701465 ? 34.8 Nm, 1701466 ? 30.4 Nm, 36336100 ? 56.0 Nm, 36336200 ? 57.9 Nm. The structure of brass samples especially in the threaded section (as required) was observed by the inverted light microscope ZEISS AXIO OBSERVER Z1m.The hardness and microhardness was measured using a LECO microhardness tester AMH43. The structure analysis of fracture surface and element analysis was performed on a scanning electron microscope JEOL JSM-7600F with an energy dispersive analyzer OXFORDX-Max 20 mm2.

Druh

O - Ostatní výsledky

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů