Removing of Brass Corrosion Layer by Hydrogen/Argon Plasma

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26310%2F14%3APU111780" target="_blank" >RIV/00216305:26310/14:PU111780 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Removing of Brass Corrosion Layer by Hydrogen/Argon Plasma

Popis výsledku v původním jazyce

Brass samples with model corrosion layers were treated in low pressure low tempereture plasma. Effects of different ratios of hydrogen/argon were compared in this work. The ratio 30 sccm hydrogen and 20 sccm argon flows (hydrogen content 60 % in volume)is the best, because the temperature of sample during treatment was the lowest and chlorides were complete removed from corrosion layer in this case.

Název v anglickém jazyce

Removing of Brass Corrosion Layer by Hydrogen/Argon Plasma

Popis výsledku anglicky

Brass samples with model corrosion layers were treated in low pressure low tempereture plasma. Effects of different ratios of hydrogen/argon were compared in this work. The ratio 30 sccm hydrogen and 20 sccm argon flows (hydrogen content 60 % in volume)is the best, because the temperature of sample during treatment was the lowest and chlorides were complete removed from corrosion layer in this case.

Druh

O - Ostatní výsledky

CEP obor

AC - Archeologie, antropologie, etnologie

OECD FORD obor

—

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů