Polymer-coated iron oxide magnetic nanoparticles ? preparation and characterization

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F11%3APU95083" target="_blank" >RIV/00216305:26620/11:PU95083 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Polymer-coated iron oxide magnetic nanoparticles ? preparation and characterization

Popis výsledku v původním jazyce

This contribution presents the production of polymer-coated iron oxide magnetic nanoparticles carrying functional groups on their surface and their basic characterization. The preparation of polymer-coated nanoparticles was carried out by a two-step process. In the first step, magnetite (Fe3O4) nanoparticles were prepared by a co-precipitation method from the solutions of FeCl2.4H2O and FeCl3.6H2O using aqueous solution of NaOH. In the second step, obtained magnetic nanoparticles were coated with polymer using emulsion polymerization at high surfactant to monomer ratio. Methyl methacrylate (MMA) and acrylic acid (AAc) were used as comonomers, sodium dodecyl sulfate (SDS) as a surfactant and potassium persulfate (KPS) as an initiator.

Název v anglickém jazyce

Polymer-coated iron oxide magnetic nanoparticles ? preparation and characterization

Popis výsledku anglicky

This contribution presents the production of polymer-coated iron oxide magnetic nanoparticles carrying functional groups on their surface and their basic characterization. The preparation of polymer-coated nanoparticles was carried out by a two-step process. In the first step, magnetite (Fe3O4) nanoparticles were prepared by a co-precipitation method from the solutions of FeCl2.4H2O and FeCl3.6H2O using aqueous solution of NaOH. In the second step, obtained magnetic nanoparticles were coated with polymer using emulsion polymerization at high surfactant to monomer ratio. Methyl methacrylate (MMA) and acrylic acid (AAc) were used as comonomers, sodium dodecyl sulfate (SDS) as a surfactant and potassium persulfate (KPS) as an initiator.

Druh

D - Stať ve sborníku

CEP obor

CF - Fyzikální chemie a teoretická chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP102%2F11%2F1068" target="_blank" >GAP102/11/1068: Nano-elektro-bio-nástroje pro biochemické a molekulárně-biologické studie eukaryotických buněk (NanoBioTECell)</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

NANOCON 2011 - sborník příspěvků

ISBN

978-80-87294-27-7

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

1-6

Název nakladatele

Tanger

Místo vydání

Neuveden

Místo konání akce

Brno

Datum konání akce

21. 9. 2011

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000306686700092