Oscillatory shear rheology of polystyrene melts filled with carbon black and fullerene

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F12%3APU100734" target="_blank" >RIV/00216305:26620/12:PU100734 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Oscillatory shear rheology of polystyrene melts filled with carbon black and fullerene

Popis výsledku v původním jazyce

Fullerene C60 and submicrometre sized particles of carbon black were used to investigate the size effect of filler particles on the rheological behaviour of polydisperse polystyrene melts. The addition of 5 wt-% carbon black increased the viscosity of all the composite melts relative to their polymer matrixes. The effect of 5 wt-% fullerene nanoparticles on the viscosity of composites depended on the molecular weight distribution of the polymer matrixes. In the polymer with a high fraction of polymer chains below the critical molecular weight for entanglement, the fullerene addition increased the viscosity, similar to carbon black addition. As the molecular weight distribution of the polymer matrix moved to higher values, the influence of fullerene addition on melt viscosity changed, and the viscosity of the nanocomposite was similar to that of the polymer matrix. The effect of fullerene addition on the melt viscosity of the coarse particle composite was also investigated.

Název v anglickém jazyce

Oscillatory shear rheology of polystyrene melts filled with carbon black and fullerene

Popis výsledku anglicky

Fullerene C60 and submicrometre sized particles of carbon black were used to investigate the size effect of filler particles on the rheological behaviour of polydisperse polystyrene melts. The addition of 5 wt-% carbon black increased the viscosity of all the composite melts relative to their polymer matrixes. The effect of 5 wt-% fullerene nanoparticles on the viscosity of composites depended on the molecular weight distribution of the polymer matrixes. In the polymer with a high fraction of polymer chains below the critical molecular weight for entanglement, the fullerene addition increased the viscosity, similar to carbon black addition. As the molecular weight distribution of the polymer matrix moved to higher values, the influence of fullerene addition on melt viscosity changed, and the viscosity of the nanocomposite was similar to that of the polymer matrix. The effect of fullerene addition on the melt viscosity of the coarse particle composite was also investigated.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JI - Kompositní materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2012

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

PLASTICS RUBBER AND COMPOSITES

ISSN

1465-8011

e-ISSN

—

Svazek periodika

41

Číslo periodika v rámci svazku

9

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

6

Strana od-do

384-389

Kód UT WoS článku

000311413100003

EID výsledku v databázi Scopus

—