Microstructural Characterisations of Slurry Aluminide Diffusion Coatings

Popis výsledku v původním jazyce

Commercially pure aluminium powder and a mixture of aluminium and silicon powders, both in a liquid amyl acetate-based organic binder, were sprayed onto the surface of Inconel 713LC nickel base superalloy. A two-stage heat treatment process in an argon atmosphere flow was designed and applied to produce nickel aluminide diffusion coatings. Two coating systems composed of different layers with gradual changes in chemical composition and phase quantities were formed. Scanning electron microscope, scanningelectron microscope/focused ion beam, both equipped with energy dispersive microanalyzers, were utilized to characterize the microstructure and chemical composition of the coatings. Introduction

Název v anglickém jazyce

Microstructural Characterisations of Slurry Aluminide Diffusion Coatings

Popis výsledku anglicky

Commercially pure aluminium powder and a mixture of aluminium and silicon powders, both in a liquid amyl acetate-based organic binder, were sprayed onto the surface of Inconel 713LC nickel base superalloy. A two-stage heat treatment process in an argon atmosphere flow was designed and applied to produce nickel aluminide diffusion coatings. Two coating systems composed of different layers with gradual changes in chemical composition and phase quantities were formed. Scanning electron microscope, scanningelectron microscope/focused ion beam, both equipped with energy dispersive microanalyzers, were utilized to characterize the microstructure and chemical composition of the coatings. Introduction

Druh

O - Ostatní výsledky

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů