Cyclic plastic behavior and fatigue life of AZ91 alloy in as-cast and ultrafine-grained state
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F14%3APU110765" target="_blank" >RIV/00216305:26620/14:PU110765 - isvavai.cz</a>
Výsledek na webu
<a href="http://ojs.mateng.sk/index.php/Mateng/article/view/143/196" target="_blank" >http://ojs.mateng.sk/index.php/Mateng/article/view/143/196</a>
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Cyclic plastic behavior and fatigue life of AZ91 alloy in as-cast and ultrafine-grained state
Popis výsledku v původním jazyce
Fatigue properties of magnesium alloy AZ91 in as-cast and in ultrafine-grained state prepared by equal channel angular pressing were investigated. The fatigue strength in the low-cycle fatigue region was found to be substantially improved by the severe plastic deformation, whereas the improvement in the high-cycle fatigue region is negligible. The cyclic plastic response in both states is qualitatively similar; short initial softening is followed by a long cyclic hardening. The observed fatigue behaviorwas discussed in terms of specific microstructural features of both states and on the basis of cyclic slip localization and fatigue crack initiation.
Název v anglickém jazyce
Cyclic plastic behavior and fatigue life of AZ91 alloy in as-cast and ultrafine-grained state
Popis výsledku anglicky
Fatigue properties of magnesium alloy AZ91 in as-cast and in ultrafine-grained state prepared by equal channel angular pressing were investigated. The fatigue strength in the low-cycle fatigue region was found to be substantially improved by the severe plastic deformation, whereas the improvement in the high-cycle fatigue region is negligible. The cyclic plastic response in both states is qualitatively similar; short initial softening is followed by a long cyclic hardening. The observed fatigue behaviorwas discussed in terms of specific microstructural features of both states and on the basis of cyclic slip localization and fatigue crack initiation.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/EE2.3.30.0039" target="_blank" >EE2.3.30.0039: Excelentní mladí vědci na VUT v Brně</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materiálové inžinierstvo
ISSN
1335-0803
e-ISSN
—
Svazek periodika
21
Číslo periodika v rámci svazku
3
Stát vydavatele periodika
SK - Slovenská republika
Počet stran výsledku
7
Strana od-do
109-115
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—