CYCLIC PLASTIC BEHAVIOR AND FATGIUE LIFE OF AZ91 ALLOY IN AS-CAST AND ULTRAFINE-GRAINED STATE

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68081723%3A_____%2F14%3A00434751" target="_blank" >RIV/68081723:_____/14:00434751 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

CYCLIC PLASTIC BEHAVIOR AND FATGIUE LIFE OF AZ91 ALLOY IN AS-CAST AND ULTRAFINE-GRAINED STATE

Popis výsledku v původním jazyce

Fatigue properties of magnesium alloy AZ91 in as-cast and in ultrafine-grained state prepared by equal channel angular pressing were investigated. The fatigue strength in the low-cycle fatigue region was found to be substantially improved by the severe plastic deformation, whereas the improvement in the high-cycle fatigue region is negligible. The cyclic plastic response in both states is qualitatively similar; short initial softening is followed by a long cyclic hardening. The observed fatigue behaviorwas discussed in terms of specific microstructural features of both states and on the basis of cyclic slip localization and fatigue crack initiation.

Název v anglickém jazyce

CYCLIC PLASTIC BEHAVIOR AND FATGIUE LIFE OF AZ91 ALLOY IN AS-CAST AND ULTRAFINE-GRAINED STATE

Popis výsledku anglicky

Fatigue properties of magnesium alloy AZ91 in as-cast and in ultrafine-grained state prepared by equal channel angular pressing were investigated. The fatigue strength in the low-cycle fatigue region was found to be substantially improved by the severe plastic deformation, whereas the improvement in the high-cycle fatigue region is negligible. The cyclic plastic response in both states is qualitatively similar; short initial softening is followed by a long cyclic hardening. The observed fatigue behaviorwas discussed in terms of specific microstructural features of both states and on the basis of cyclic slip localization and fatigue crack initiation.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/7AMB14SK064" target="_blank" >7AMB14SK064: Vysokocyklová a gigacyklová únava ultrajemnozrnných materiálů připravených intenzivní plastickou deformací</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materiálové inžinierstvo - Materials Engineering

ISSN

1335-0803

e-ISSN

—

Svazek periodika

21

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

7

Strana od-do

109-115

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—