A fractographic study of bending/torsion fatigue failure in metallic materials with protective surface layers
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F16%3APU119721" target="_blank" >RIV/00216305:26620/16:PU119721 - isvavai.cz</a>
Výsledek na webu
<a href="https://www.hindawi.com/journals/amse/2016/8952657/" target="_blank" >https://www.hindawi.com/journals/amse/2016/8952657/</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1155/2016/8952657" target="_blank" >10.1155/2016/8952657</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
A fractographic study of bending/torsion fatigue failure in metallic materials with protective surface layers
Popis výsledku v původním jazyce
Results are given of a fractographic study of biaxial in-phase bending/torsion fatigue fractures in specimens made of nitrided steel and nickel-based superalloy with protective coatings (diffusion coatings and plasma-sprayed thermal barrier coatings). Fracture surfaces were examined by optical and scanning electron microscopes while stereophotogrammetry and optical profilometry were employed to obtain 3D surface data of selected fracture surface regions. The studied materials exhibited a wide range of fracture mechanisms depending on the microstructure and applied mechanical loading.
Název v anglickém jazyce
A fractographic study of bending/torsion fatigue failure in metallic materials with protective surface layers
Popis výsledku anglicky
Results are given of a fractographic study of biaxial in-phase bending/torsion fatigue fractures in specimens made of nitrided steel and nickel-based superalloy with protective coatings (diffusion coatings and plasma-sprayed thermal barrier coatings). Fracture surfaces were examined by optical and scanning electron microscopes while stereophotogrammetry and optical profilometry were employed to obtain 3D surface data of selected fracture surface regions. The studied materials exhibited a wide range of fracture mechanisms depending on the microstructure and applied mechanical loading.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20306 - Audio engineering, reliability analysis
Návaznosti výsledku
Projekt
<a href="/cs/project/LQ1601" target="_blank" >LQ1601: CEITEC 2020</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2016
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Advances in Materials Science and Engineering
ISSN
1687-8434
e-ISSN
1687-8442
Svazek periodika
2016
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
6
Strana od-do
1-6
Kód UT WoS článku
000378290400001
EID výsledku v databázi Scopus
2-s2.0-84976514069